Ultramid® B3WG7 BK00564
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | BASF Corporation |
| Trademark: | Ultramid® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXKf91_Ultramid-B3WG7-BK00564.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Ultramid B3WG7 BK00564 is a 35% glass fiber reinforced, pigmented black, injection molding PA6 grade for highly rigid, dimensionally stable components which are resistant to high temperature aging and have improved retention of properties in a hot water environment. Applications Typical applications include automotive clutch and accelerator pedals. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.41 | -- | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | |||
| Saturation, 23°C | 6.2 | -- | % | |
| Equilibrium, 23°C, 50% RH | 2.0 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 11000 | -- | MPa | ISO 527-2 |
| Tensile Stress (Break, 23°C) | 188 | -- | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 3.0 | -- | % | ISO 527-2 |
| Flexural Modulus (23°C) | 10000 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 12 | -- | kJ/m² | ISO 179 |
| Notched Izod Impact Strength (23°C) | 12 | -- | kJ/m² | ISO 180 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 215 | -- | °C | ISO 75-2/A |
| Melting Temperature (DSC) | 220 | -- | °C | ISO 3146 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+13 | 1.0E+10 | ohms·cm | IEC 60093 |
| Dielectric Constant (1 MHz) | 3.90 | 6.20 | IEC 60250 | |
| Dissipation Factor | IEC 60250 | |||
| 100 Hz | 0.021 | 0.19 | ||
| 1 MHz | 0.021 | 0.19 | ||
| Comparative Tracking Index | 450 | 450 | V | IEC 60112 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 83.0 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.15 | % | |
| Processing (Melt) Temp | 270 to 295 | °C | |
| Mold Temperature | 80.0 to 95.0 | °C | |
| Injection Pressure | 3.50 to 12.5 | MPa | |
| Injection Rate | Fast |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ALTECH® PBT A 1000/100 | ALBIS PLASTIC GmbH | PBT | ALTECH® PBT |
| Crastin® HR5315HF NC010 | DuPont Performance Polymers | PBT | Crastin® |
| Iupilon® MB2212R | Mitsubishi Engineering-Plastics Corp | PC+ABS | Iupilon® |
| Karina COMP. PVC CRYSTAL - E 90/212-DA-IS-SI-AT | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LUVOCOM® 1/XCF/20-OS | Lehmann & Voss & Co. | Nylon 66 | LUVOCOM® |