Mytex® AS171L-02US
| Category: | TPO , Compounded Polypropylene |
| Manufacturer: | Mytex Polymers |
| Trademark: | Mytex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vXAnvz_Mytex-AS171L-02US.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| AS171L-02US is a compunded thermoplastics polyolefin (TPO) designed for exterior automotive applications requiring cold temperature impact, processability and paintability. This product is available in natural and black. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.980 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) 1(230°C/2.16 kg) | 24 | g/10 min | ISO 1133 |
| Molding Shrinkage 2 | ISO 294-4 | ||
| -- | 5.0E-3 to 7.0E-3 | % | |
| 80°C, 1 hr | 6.0E-3 to 8.0E-3 | % | |
| 121°C, 1 hr | 7.0E-3 to 9.0E-3 | % | |
| Ash Content (600°C) | 13.0 | wt% | ISO 3451-1A |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 15.0 | MPa | ISO 527-2/1A/50 |
| Flexural Modulus - Chord 3(23°C) | 1100 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact Strength (23°C) | 54 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 50.0 | °C | ISO 75-2/Af |
| Note Message | |
|---|---|
| 1 . | Procedure B |
| 2 . | 48 hrs after molding |
| 3 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| VinyLoop® FP001 | Vinyloop Ferrara S.p.A. | PVC, Unspecified | VinyLoop® |
| U-polymer UM-8400-20 | UNITIKA Plastics Division | Polyarylate | U-polymer |
| Chemraz 592 | Greene, Tweed & Co. | Perfluoroelastomer | Chemraz |
| EXCELINK 2700B | JSR Corporation | TPV | EXCELINK |
| MAJORIS DFR110 | AD majoris | PP, Unspecified | MAJORIS |