CALIBRE™ 2061-22

Category:	PC , Polycarbonate Resin
Manufacturer:	Trinseo
Trademark:	CALIBRE™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vWq1ME_CALIBRE-2061-22.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

CALIBRE™ 2061-22 resin is suitable for steam and ethylene oxide sterilization required by the health care industry. CALIBRE 2061-22 provides exceptional clarity, heat resistance, impact strength and processability, and has low contamination levels. CALIBRE 2061-22 resin has undergone biocompatibility testing based on ISO 10993 (Biological Evaluation of Medical Devices) and is suitable for use in approved medical applications. This product contains mold release.

Main Characteristics:

Tested under ISO 10993

Applications:

Medical applications

General Information
Additive	Mold Release
Features	Biocompatible Ethylene Oxide Sterilizable Good Processability High Clarity High Heat Resistance High Impact Resistance Steam Sterilizable
Uses	Medical/Healthcare Applications
Agency Ratings	ISO 10993 3
Forms	Pellets
Processing Method	Injection Molding
Multi-Point Data	Specific Heat vs. Temperature (ASTM D3417) Specific Volume vs Temperature (ISO 11403-2) Tensile Stress vs. Strain (ASTM D638) Thermal Conductivity vs. Temperature (ASTM E1530)

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.20	g/cm³	ASTM D792, ISO 1183/B
Melt Mass-Flow Rate (MFR) (300°C/1.2 kg)	22	g/10 min	ASTM D1238, ISO 1133
Water Absorption			ASTM D570, ISO 62
23°C, 24 hr	0.15	%
Equilibrium, 23°C, 50% RH	0.32	%

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (R-Scale)	118		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Modulus
-- ¹	2340	MPa	ASTM D638
--	2340	MPa	ISO 527-2/50
Tensile Strength
Yield ²	60.0	MPa	ASTM D638
Yield	60.0	MPa	ISO 527-2/50
Break ³	65.5	MPa	ASTM D638
Break	66.0	MPa	ISO 527-2/50
Tensile Elongation
Break ⁴	120	%	ASTM D638
Break	120	%	ISO 527-2/50
Flexural Modulus
-- ⁵	2410	MPa	ASTM D790
-- ⁶	2410	MPa	ISO 178
Flexural Strength
-- ⁷	96.5	MPa	ASTM D790
-- ⁸	96.5	MPa	ISO 178
Taber Abrasion Resistance	45	%	ASTM D1044

Flammability	Nominal Value	Unit	Test Method
Average Extent of Burning	3	cm	ASTM D635

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact
23°C	750	J/m	ASTM D256
23°C	73	kJ/m²	ISO 180/A
Instrumented Dart Impact ⁹(23°C, Total Energy)	72.3	J	ASTM D3763

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load
0.45 MPa, Annealed	142	°C	ASTM D648, ISO 75-2/B
1.8 MPa, Unannealed	126	°C	ASTM D648, ISO 75-2/A
1.8 MPa, Annealed	126	°C	ASTM D648, ISO 75-2/A
Vicat Softening Temperature	152	°C	ISO 306/B50, ASTM D1525 ¹⁰
CLTE - Flow (-40 to 82°C)	6.8E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value	Unit	Test Method
Volume Resistivity	2.0E+17	ohms·cm	ASTM D257
Dielectric Strength	17	kV/mm	ASTM D149, IEC 60243-1
Dielectric Constant			ASTM D150
60 Hz	3.00
1 MHz	3.00
Dissipation Factor			ASTM D150
50 Hz	1.0E-3
1 MHz	2.0E-3

Flammability	Nominal Value	Unit	Test Method
Flame Rating			UL 94
1.50 mm ¹¹	HB
3.00 mm	HB
0.750 mm	V-2
1.50 mm	V-2

Optical	Nominal Value	Unit	Test Method
Refractive Index	1.586		ASTM D542, ISO 489
Transmittance	89.0	%	ASTM D1003
Haze	1.0	%	ASTM D1003

Note Message
1 .	50 mm/min
2 .	50 mm/min
3 .	50 mm/min
4 .	50 mm/min
5 .	Method I (3 point load), 2.0 mm/min
6 .	2.0 mm/min
7 .	Method I (3 point load), 2.0 mm/min
8 .	2.0 mm/min
9 .	3.39 m/sec
10 .	Rate A (50°C/h), Loading 2 (50 N)
11 .	This rating not intended to reflect hazards presented by this or any other material under actual fire conditions.

Resin Grade	Manufacturer	Category	Trademark
RTP 2200 LF	RTP Company	PEEK	RTP
Conpol™ 5B10S1	DuPont Packaging & Industrial Polymers	EMAA	Conpol™
EMOPLEN® CP GFR 10	EMAS Plastik San.Tic.AS.	PP Copolymer	EMOPLEN®
Karina COOL GRAY -E831-28/16-Y-ERYB-LMP	Karina Ind. e Com. de Plásticos Ltda	PVC, Unspecified	Karina
POLYFORT® FPP 20 GFM HI	A. Schulman Europe	PP Homopolymer	POLYFORT®