Vyncolit SI 9041 is a silicone (Silicone) material containing long glass fiber. This product is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. The processing method is: resin transfer molding or compression molding. The main characteristics of Vyncolit SI 9041 are: impact resistance. Typical application areas include: Electrical/electronic applications Wire and cable military applications

General Information
Filler / Reinforcement	Long glass fiber
Features	Impact resistance, high Good electrical performance
Uses	Electronic insulation Military application Connector
Agency Ratings	ASTM D 5948, Type MSI-30
Forms	flake
Processing Method	Resin transfer molding Compression molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.30	g/cm³	ASTM D792
Bulk Factor	7.0		ASTM D1895
Molding Shrinkage - Flow (Compression Molded)	0.010 - 0.10	%	ASTM D955
Water Absorption (23°C, 24 hr)	0.15	%	ASTM D570

Hardness	Nominal Value	Unit	Test Method
Rockwell Hardness (M-Scale)	90		ASTM D785

Mechanical	Nominal Value	Unit	Test Method
Tensile Strength	27.6	MPa	ASTM D638
Flexural Modulus	13800	MPa	ASTM D790
Flexural Strength	68.9	MPa	ASTM D790
Compressive Strength	75.8	MPa	ASTM D695

Impact	Nominal Value	Unit	Test Method
Notched Izod Impact	270	J/m	ASTM D256A

Thermal	Nominal Value	Unit	Test Method
Deflection Temperature Under Load (1.8 MPa, Unannealed)	288	°C	ASTM D648

Electrical	Nominal Value	Unit	Test Method
Dielectric Strength			ASTM D149
-- ¹	5.9	kV/mm	ASTM D149
-- ²	3.9	kV/mm	ASTM D149
Arc Resistance	210	sec	ASTM D495

Additional Information
Water Absorption, ASTM D570, 48 hrs, 50°C: 0.4%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 150 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 100 V/milBulk Factor, ASTM D1895: 6 to 8Compression and Transfer Molding Conditions: Preheat Temperature: 150 to 180 °F Mold Temperature: 280 to 300 °F Compression Mold Pressure: 2000 to 6000 psi Transfer Mold Pressure: 4000 to 8000 psi Cure Time, 0.125 in: 300 sec

Additional Information

Water Absorption, ASTM D570, 48 hrs, 50°C: 0.4%Dielectric Strength, ASTM D149, 60 Hz, Method A, wet: 150 V/milDielectric Strength, ASTM D149, 60 Hz, Method B, wet: 100 V/milBulk Factor, ASTM D1895: 6 to 8Compression and Transfer Molding Conditions: Preheat Temperature: 150 to 180 °F Mold Temperature: 280 to 300 °F Compression Mold Pressure: 2000 to 6000 psi Transfer Mold Pressure: 4000 to 8000 psi Cure Time, 0.125 in: 300 sec

Note Message
1 .	Method A (short time)
2 .	Method B (step by step)

Category:	Silicone , Silicone
Manufacturer:	Vyncolit N.V.
Trademark:	Vyncolit®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vWerXi_Vyncolit-SI-9041.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
MARCOBLEND AU 111	POLY GIN	PC+PET	MARCOBLEND
RTP ESD A 2700-45A	RTP Company	TPE	RTP
Shuman PS SP810	Shuman Plastics, Inc.	PS (HIPS)	Shuman PS
AMTOPP PL40	Inteplast Group	PP, Unspecified	AMTOPP
ESTASTIR HI 0408 V0	Cossa Polimeri S.r.l.	PS (HIPS)	ESTASTIR