Durethan® DP A 30 S FN30 DUS025 000000
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | LANXESS Asia/Pacific |
| Trademark: | Durethan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vVNkXi_Durethan-DP-A-30-S-FN30-DUS025-000000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| PA 66, non-reinforced, injection molding, halogen free flame retardant, improved flowability |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| Processing Method |
|
| Resin ID (ISO 1043) |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.17 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 2577 | |||
| Across Flow : 270°C, 2.00 mm 1 | 1.1 | -- | % | |
| Across Flow : 120°C, 4 hr, 2.00 mm 2 | 0.10 | -- | % | |
| Flow : 270°C, 2.00 mm 3 | 1.1 | -- | % | |
| Flow : 120°C, 4 hr, 2.00 mm 4 | 0.10 | -- | % |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus (23°C) | 3800 | 1500 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield, 23°C) | 85.0 | 50.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 23°C) | 4.1 | > 20 | % | ISO 527-2/50 |
| Flexural Modulus 5(23°C) | 3900 | 1600 | MPa | ISO 178/A |
| Flexural Stress | ISO 178/A | |||
| 3.5% Strain, 23°C | 115 | 40.0 | MPa | |
| 23°C 6 | 135 | 55.0 | MPa | |
| Flexural Strain at Flexural Strength 7(23°C) | 5.8 | 8.0 | % | ISO 178/A |
| Additional Information | Dry | Conditioned | Test Method | |
|---|---|---|---|---|
| ISO Shortname | PA 66, GF, 14-040 | -- | ISO 1874 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Residual Moisture Content | 0.030 to 0.070 | % | Karl Fisher |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | < 10 | < 10 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 50 | 80 | kJ/m² | |
| 23°C | 60 kJ/m² | No Break | ||
| Notched Izod Impact Strength (23°C) | < 10 | < 10 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength | ISO 180/1U | |||
| -30°C | 45 | 55 | kJ/m² | |
| 23°C | 45 kJ/m² | No Break |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, Unannealed | 212 | -- | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 80.0 | -- | °C | ISO 75-2/A |
| Vicat Softening Temperature | 230 | -- | °C | ISO 306/B120 |
| Melting Temperature 8 | 265 | -- | °C | ISO 11357-3 |
| CLTE | ISO 11359-2 | |||
| Flow : 23 to 55°C | 8.0E-5 | -- | cm/cm/°C | |
| Transverse : 23 to 55°C | 7.0E-5 | -- | cm/cm/°C |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Comparative Tracking Index (Solution A) | 600 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.400 mm) | V-0 | -- | UL 94 | |
| Glow Wire Flammability Index (0.400 mm) | 960 | -- | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature (0.400 mm) | 775 | -- | °C | IEC 60695-2-13 |
| Oxygen Index 9 | 35 | -- | % | ISO 4589-2 |
| Injection | Dry | Unit | Test Method |
|---|---|---|---|
| Drying Temperature - Dry Air Dryer | 80.0 | °C | |
| Drying Time - Dry Air Dryer | 2.0 to 6.0 | hr | |
| Processing (Melt) Temp | 260 to 270 | °C | |
| Mold Temperature | 80.0 to 100 | °C |
| Note Message | |
|---|---|
| 1 . | 60x60x2mm, 80°C MT, 600 bar |
| 2 . | 60x60x2mm |
| 3 . | 60x60x2mm, 80°C MT, 600 bar |
| 4 . | 60x60x2mm |
| 5 . | 2.0 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2 mm/min |
| 8 . | 10°C/min |
| 9 . | Procedure A |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Purell HP671T | LyondellBasell Industries | PP Homopolymer | Purell |
| Skyrol® SR50 | SKC Inc. | PET | Skyrol® |
| Novodur® 450 | Styrolution | ABS | Novodur® |
| Petrothene® NA952000 | LyondellBasell Industries | LDPE | Petrothene® |
| MARPOL® COPP 20.4 | Marco Polo International, Inc. | PP Impact Copolymer | MARPOL® COPP |