Elastoflex® 28100R Resin / 28100T Isocyanate

Category:	PUR-MDI , Polyurethane (MDI)
Manufacturer:	BASF Corporation
Trademark:	Elastoflex®
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vV76WN_Elastoflex28100RResin28100TIsocyanate.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

Message
An MDI-based, low-emissions foam system designed for automotive flexible foam applications.

General Information
Features	Low volatilization Good flexibility
Uses	Foam Application in Automobile Field

Physical	Nominal Value	Unit
Specific Gravity
Matrix resin	1.03	g/cm³
Hardener ¹	1.21	g/cm³

Additional Information
Physical constants: Specific gravity, resin at 25°C: 1.025 g/cm³ Specific gravity, isocyanate at 25°C: 1.206 g/cm³ Viscosity, resin at 25°C: 1390 cP Viscosity, isocyanate at 25°C: 94 cP Processing parameters: Mix Ratio - Parts by weight at 100 Index, Iso : Resin: 1.025 Component temperatures: 24 to 32°C Demold Time: 3 to 4 min Mix pressure: 130 to 160 bar Mold Temperature: 54 to 63°C High pressure machine reactivity: Cream Time: 10 sec String gel time: 61 sec Rise time: 77 sec Free rise density: 37.9 kg/m³

Additional Information

Physical constants: Specific gravity, resin at 25°C: 1.025 g/cm³ Specific gravity, isocyanate at 25°C: 1.206 g/cm³ Viscosity, resin at 25°C: 1390 cP Viscosity, isocyanate at 25°C: 94 cP Processing parameters: Mix Ratio - Parts by weight at 100 Index, Iso : Resin: 1.025 Component temperatures: 24 to 32°C Demold Time: 3 to 4 min Mix pressure: 130 to 160 bar Mold Temperature: 54 to 63°C High pressure machine reactivity: Cream Time: 10 sec String gel time: 61 sec Rise time: 77 sec Free rise density: 37.9 kg/m³

Note Message
1 .	Isocyanate

Resin Grade	Manufacturer	Category	Trademark
4LEX® 10F13301	4Plas	PC	4LEX®
BioFibra® BF-LUD01	FuturaMat	Biodeg Polymers	BioFibra®
Boltaron 4325 FM4910 Clear CPVC	Boltaron Performance Products	CPVC	Boltaron
Braskem PE PB-682	Braskem	LDPE	Braskem PE
ULTEM™ 2200R resin	SABIC Innovative Plastics	PEI	ULTEM™