Trexlink™ 6760
| Category: | TPE , Thermoplastic Elastomer |
| Manufacturer: | Mitsubishi Chemical Performance Polymers, Inc. |
| Trademark: | Trexlink™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vUVP7C_Trexlink-6760.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Trexlink ™ 6760 is a highly engineered Thermoplastic Elastomer for use in applications requiring integrally colored material. This material is UV stabilized and can be pre-colored in most Automotive Interior or other colors. It can be easily processed by injection molding, or blow molding. Applications include critical color matched Automotive components such cup holders, mats, seals, soft seat trim. Also works well for two-shot molding or over-mold components such as grips and handles. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.910 | g/cm³ | ISO 1183 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A, 5 sec, Injection Molded) | 65 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress - Across Flow 1(100% Strain) | 2.40 | MPa | ISO 37 |
| Tensile Stress - Across Flow 2(Yield) | 5.30 | MPa | ISO 37 |
| Tensile Elongation - Across Flow 3(Break) | 550 | % | ISO 37 |
| Tear Strength - Across Flow 4 | 21 | kN/m | ISO 34-1 |
| Compression Set 5(70°C, 22 hr) | 35 | % | ISO 815 |
| Aging | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Change in Tensile Strength in Air 6(135°C, 1000 hr) | -20 | % | ISO 188 |
| Change in Tensile Strain at Break in Air 7(135°C, 1000 hr) | -20 | % | ISO 188 |
| Additional Information |
|---|
| Change in Color, SAE J1885, 1240.8kJ/m² exposure: <3.0 delta E |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 177 - 216 | °C | |
| Middle Temperature | 177 - 216 | °C | |
| Front Temperature | 177 - 216 | °C | |
| Nozzle Temperature | 188 - 221 | °C | |
| Processing (Melt) Temp | 182 - 221 | °C | |
| Mold Temperature | 10.0 - 65.6 | °C | |
| Back Pressure | 0.0689 - 1.03 | MPa | |
| Screw Speed | 100 - 200 | rpm | |
| Screw L/D Ratio | 20.0:1.0 |
| Note Message | |
|---|---|
| 1 . | Type 1 |
| 2 . | Type 1 |
| 3 . | Type 1 |
| 4 . | Method B, right-angle specimen (cut) |
| 5 . | Type a |
| 6 . | Method B |
| 7 . | Method B |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Propafilm™ RXP125 | Innovia Films Ltd. | PP Alloy | Propafilm™ |
| Acculam™ Phenolfab Canvas | Accurate Plastics, Inc. | Phenolic | Acculam™ |
| Envirez® 50483 | Ashland Performance Materials | Polyester, TS | Envirez® |
| Hostacom TBC 172N | LyondellBasell Industries | PP Copolymer | Hostacom |
| Huafon T26P | Huafon Group Co., Ltd. | Nylon 66 | Huafon |