CYCOLAC™ DL100 resin
| Category: | ABS , Acrylonitrile Butadiene Styrene |
| Manufacturer: | SABIC Innovative Plastics Europe |
| Trademark: | CYCOLAC™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vTIeoV_CYCOLACDL100resin.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
CYCOLAC DL100 is a high heat, high impact, low emissions ABS/PC blend. |
| General Information | |
|---|---|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.08 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 7.0 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (260°C/5.0 kg) | 8.00 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow 1 | 0.50 - 0.70 | % | Internal method |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 104 | ASTM D785 | |
| Ball Indentation Hardness (H 358/30) | 91.0 | MPa | ISO 2039-1 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 2 | 2240 | MPa | ASTM D638 |
| -- | 2200 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 3 | 44.0 | MPa | ASTM D638 |
| Yield | 46.0 | MPa | ISO 527-2/5 |
| Yield | 45.0 | MPa | ISO 527-2/50 |
| Tensile Strain | |||
| Yield | 3.5 | % | ISO 527-2/5 |
| Yield | 3.4 | % | ISO 527-2/50 |
| Fracture 4 | 90 | % | ASTM D638 |
| Fracture | 60 | % | ISO 527-2/5 |
| Fracture | 10 | % | ISO 527-2/50 |
| Flexural Modulus 5 | 2260 | MPa | ISO 178 |
| Flexural Stress | 69.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 6 | ISO 179/1eA | ||
| -30°C | 14 | kJ/m² | ISO 179/1eA |
| 23°C | 34 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| 23°C | 700 | J/m | ASTM D256 |
| 23°C, 6.40 mm | 550 | J/m | ASTM D256 |
| -30°C 7 | 15 | kJ/m² | ISO 180/1A |
| 23°C 8 | 35 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 105 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 100 mm span 9 | 104 | °C | ISO 75-2/Be |
| 1.8 MPa, unannealed, 3.20mm | 88.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 6.40mm | 90.0 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 100 mm span 10 | 87.0 | °C | ISO 75-2/Ae |
| Vicat Softening Temperature | |||
| -- | 105 | °C | ISO 306/B50 |
| -- | 107 | °C | ISO 306/B120 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow : 23 to 60°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| Lateral : 23 to 60°C | 9.8E-5 | cm/cm/°C | ISO 11359-2 |
| RTI Elec | 60.0 | °C | UL 746 |
| RTI Imp | 60.0 | °C | UL 746 |
| RTI | 60.0 | °C | UL 746 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | UL 94 | |
| 3.00 mm | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 90.0 - 100 | °C | |
| Drying Time | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.10 | % | |
| Hopper Temperature | 60.0 - 80.0 | °C | |
| Rear Temperature | 230 - 260 | °C | |
| Middle Temperature | 250 - 280 | °C | |
| Front Temperature | 250 - 280 | °C | |
| Nozzle Temperature | 245 - 275 | °C | |
| Processing (Melt) Temp | 250 - 280 | °C | |
| Mold Temperature | 40.0 - 80.0 | °C |
| Note Message | |
|---|---|
| 1 . | Tensile Bar |
| 2 . | 5.0 mm/min |
| 3 . | Type 1, 5.0 mm/min |
| 4 . | Type 1, 5.0 mm/min |
| 5 . | 2.0 mm/min |
| 6 . | 80*10*4 sp=62mm |
| 7 . | 80*10*4 |
| 8 . | 80*10*4 |
| 9 . | 120*10*4 mm |
| 10 . | 120*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SCHULADUR® E-12672 | A. Schulman Inc. | PBT | SCHULADUR® |
| SPESIN® KP213G15BL | Kolon Plastics, Inc. | PBT | SPESIN® |
| UmaPET COMH | Ester Industries Ltd. | PET | UmaPET |
| Polifor® L3 GF/30 NATURALE | SO.F.TER. SPA | PP Homopolymer | Polifor® |
| POCAN® B 1205 XF 000000 | LANXESS Asia/Pacific | PBT | POCAN® |