SUPREME Specialty PS SP253
| Category: | PS (Specialty) , Specialty Polystyrene |
| Manufacturer: | Supreme Petrochem Ltd. |
| Trademark: | SUPREME Specialty PS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vT9SXh_SUPREME-Specialty-PS-SP253.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Toughened Polystyrene Characteristics:
Processing:
Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.02 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (200°C/5.0 kg) | 6.0 | g/10 min | ASTM D1238 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(23°C, 3.20 mm, Injection Molded) | 43.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break, 23°C, 3.20 mm, Injection Molded) | 5.0 | % | ASTM D638 |
| Flexural Modulus (23°C, 3.20 mm, Injection Molded) | 2200 | MPa | ASTM D790 |
| Flexural Strength (23°C, 3.20 mm, Injection Molded) | 60.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm, Injection Molded) | 15 | J/m | ASTM D256 |
| Unnotched Izod Impact (23°C, 3.20 mm) | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm, Injection Molded) | 81.0 | °C | ASTM D648 |
| Vicat Softening Temperature | 103 | °C | ASTM D1525 3 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.60 mm) | HB | UL 94 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Transmittance (1000 µm) | 88.0 | % | ASTM D1003 |
| Haze (1000 µm, Injection Molded) | 2.5 | % | ASTM D1003 |
| Additional Information |
|---|
| The value listed as Haze, ASTM D1003 may not have been tested according to this standard.The value listed as Transmittance, ASTM D1003 may not have been tested according to this standard. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Processing (Melt) Temp | 220 | °C | |
| Mold Temperature | 40.0 - 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 标准 B (120°C/h), 压 力1 (10N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAC® PA-756 | CHI MEI CORPORATION | ABS | POLYLAC® |
| Shuman PS 881 | Shuman Plastics, Inc. | PS (MIPS) | Shuman PS |
| Globalene® HP600S | Lee Chang Yung Chemical Industry Corp. | PP Homopolymer | Globalene® |
| Hostacom RE701C | LyondellBasell Industries | PP Copolymer | Hostacom |
| Domamid HT™ 7750R30H3 | Technical Polymers, LLC | Nylon 66 | Domamid HT™ |