Bergadur™ PB400 H UF UV BK701
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | PolyOne Corporation |
| Trademark: | Bergadur™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vT3OIg_Bergadur-PB400-H-UF-UV-BK701.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Halogen free flame retardant, with UV resistance and UL listed |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.31 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 1.2 - 1.7 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | 38.0 | MPa | ASTM D638 |
| Flexural Modulus 2 | 2850 | MPa | ASTM D790 |
| Flexural Strength 3 | 72.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 3.20 mm) | 27 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed, 3.20 mm) | 172 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Comparative Tracking Index | > 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (1.50 mm) | V-0 | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 110 - 130 | °C | |
| Drying Time | 4.0 - 6.0 | hr | |
| Rear Temperature | 240 - 270 | °C | |
| Middle Temperature | 240 - 270 | °C | |
| Front Temperature | 240 - 270 | °C | |
| Mold Temperature | 75.0 - 95.0 | °C |
| Injection instructions |
|---|
| Injection Pressure: MED-HIGHHold Pressure: MED-HIGHScrew Speed: MODERATEBack Pressure: LOW |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYFORT® FPP LGF 40 | A. Schulman Europe | PP Homopolymer | POLYFORT® |
| TOYOBO Urethane A3064D | TOYOBO America, Inc. | PUR-Ether | TOYOBO Urethane |
| NORYL™ FNH2160 resin | SABIC Innovative Plastics | PPE+PS | NORYL™ |
| Generic PPS, Linear | Generic | PPS, Linear | Generic |
| LEXAN™ PC1000R resin | SABIC Innovative Plastics | PC | LEXAN™ |