LNP™ STAT-KON™ REL42 compound
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vSagxV_LNPSTATKONREL42compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON REL42 is a compound based on Nylon 66 resin containing PTFE, Carbon Fiber. Added features of this material include: Electrically Conductive, Internally Lubricated. Also known as: LNP* STAT-KON* Compound RCL-4042 Product reorder name: REL42 |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.32 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage | |||
| Flow : 24 hours | 0.30 - 0.50 | % | ASTM D955 |
| Transverse flow : 24 hours | 1.1 - 1.3 | % | ASTM D955 |
| Vertical flow direction : 24 hours | 1.2 | % | ISO 294-4 |
| Flow direction : 24 hours | 0.36 | % | ISO 294-4 |
| Water Absorption (24 hr, 50% RH) | 0.60 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 8270 | MPa | ASTM D638 |
| -- | 8690 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield | 132 | MPa | ASTM D638 |
| Yield | 133 | MPa | ISO 527-2 |
| Fracture | 132 | MPa | ASTM D638 |
| Fracture | 133 | MPa | ISO 527-2 |
| Tensile Elongation | |||
| Yield | 2.5 | % | ASTM D638 |
| Yield | 2.3 | % | ISO 527-2 |
| Fracture | 2.5 | % | ASTM D638 |
| Fracture | 2.3 | % | ISO 527-2 |
| Flexural Modulus | |||
| -- | 14500 | MPa | ASTM D790 |
| -- | 7400 | MPa | ISO 178 |
| Flexural Strength | 186 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 43 | J/m | ASTM D256 |
| 23°C 2 | 4.6 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact | |||
| 23°C | 440 | J/m | ASTM D4812 |
| 23°C 3 | 30 | kJ/m² | ISO 180/1U |
| Instrumented Dart Impact | |||
| 23°C, Energy at Peak Load | 8.30 | J | ASTM D3763 |
| -- | 1.70 | J | ISO 6603-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 3.20mm | 260 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 64.0mm span 4 | 258 | °C | ISO 75-2/Bf |
| 1.8 MPa, unannealed, 3.20mm | 247 | °C | ASTM D648 |
| 1.8 MPa, unannealed, 64.0mm span 5 | 242 | °C | ISO 75-2/Af |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : -40 to 40°C | 7.9E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Lateral : -40 to 40°C | 3.6E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.2 | °C | |
| Drying Time | 4.0 | hr | |
| Suggested Max Moisture | 0.15 - 0.25 | % | |
| Rear Temperature | 266 - 277 | °C | |
| Middle Temperature | 282 - 293 | °C | |
| Front Temperature | 293 - 304 | °C | |
| Processing (Melt) Temp | 282 - 304 | °C | |
| Mold Temperature | 93.3 - 110 | °C | |
| Back Pressure | 0.172 - 0.344 | MPa | |
| Screw Speed | 30 - 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 80*10*4 |
| 3 . | 80*10*4 |
| 4 . | 80*10*4 mm |
| 5 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 383 FR | RTP Company | PC | RTP |
| TEREZ PC/ASA Blend 1000 | TER HELL PLASTIC GMBH | ASA+PC | TEREZ PC/ASA |
| FRAGOM LC/3013 RR | Crosspolimeri S.p.A. | Polyolefin, Unspecified | FRAGOM |
| Hipolyene 8015 FRC | Zylog Plastalloys | TPO (POE) | Hipolyene |
| Petrotene® PP A2 T30 PRTA011 PH201 | Petropol Industry and Trade of Polymers LTDA | PP Homopolymer | Petrotene® PP |