Amilan® CM3004-V0
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Toray Resin Company |
| Trademark: | Amilan® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vRlNnQ_Amilan-CM3004-V0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Amilan® CM3004-V0 is a Polyamide 66 (Nylon 66) product. It is available in Asia Pacific, Europe, or North America. Characteristics include:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Part Marking Code |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density (23°C) | 1.19 | -- | g/cm³ | ISO 1183 |
| Molding Shrinkage - Flow | Internal Method | |||
| 1.00 mm 1 | 0.60 to 0.90 | 0.60 to 0.90 | % | |
| 3.00 mm 2 | 1.0 to 1.6 | 1.0 to 1.6 | % | |
| Water Absorption | ISO 62 | |||
| 23°C, 24 hr | 1.1 | -- | % | |
| Saturation, 23°C | 7.5 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness (R-Scale, 23°C) | 120 | -- | ISO 2039-2 |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Stress | ISO 527-2 | |||
| 23°C | 85.0 | 65.0 | MPa | |
| 80°C | 45.0 | -- | MPa | |
| Tensile Strain (Break, 23°C) | 7.5 | 7.5 | % | ISO 527-2 |
| Flexural Modulus | ISO 178 | |||
| 23°C | 3500 | 1500 | MPa | |
| 80°C | 1200 | -- | MPa | |
| Flexural Stress | ISO 178 | |||
| -40°C | 170 | -- | MPa | |
| 23°C | 125 | 70.0 | MPa | |
| 80°C | 65.0 | -- | MPa | |
| Taber Abrasion Resistance (1000 Cycles) | 9.00 to 10.0 | -- | mg | ISO 9352 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | |||
| -40°C | 4.5 | -- | kJ/m² | |
| 23°C | 4.5 | 13 | kJ/m² | |
| Charpy Unnotched Impact Strength (-40°C) | 140 kJ/m² | No Break | ISO 179 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 244 | -- | °C | ISO 75-2/B |
| Melting Temperature | 265 | -- | °C | DSC |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Volume Resistivity | 1.0E+15 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 28 | -- | kV/mm | IEC 60243-1 |
| Dielectric Constant 3(23°C, 50 Hz) | 5.20 | -- | IEC 60250 | |
| Dissipation Factor 4(23°C, 50 Hz) | 0.070 | -- | IEC 60250 | |
| Arc Resistance 5 | 127 | -- | sec | UL 746 |
| Comparative Tracking Index (CTI) | 600 | -- | V | UL 746 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.397 mm) | V-0 | -- | UL 94 |
| Note Message | |
|---|---|
| 1 . | 80x80x1mm |
| 2 . | 80x80x3mm |
| 3 . | 60% RH |
| 4 . | 60% RH |
| 5 . | Tungsten Electrode |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Telcar® TL-2448G | Teknor Apex Company | TPE | Telcar® |
| TEREZ PA 6 7500 GFN 30 | TER HELL PLASTIC GMBH | Nylon 6 | TEREZ PA 6 |
| Dryflex® WS 30M500 | ELASTO | TPE | Dryflex® |
| MAJORIS DT407 - 7782 | AD majoris | PP, Unspecified | MAJORIS |
| Integra™ PEI1000HF | PolySource, LLC | PEI | Integra™ |