SABIC® PP CPC04C
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vRYhYX_SABIC-PP-CPC04C.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PP CPC04C is our newest development is our CLEARPACT range. In this new type of PP material, we combined impact resistance and stiffness of a regular block copolymer with a transparency level of typical random copolymers. These polymer properties combined with it's formulation of processing and antistatic additives makes this a unique material in the market. SABIC® PP CPC04C is typically used in various thermoforming processes for food packaging. Our customers use this material in the production of MAP-trays and packaging for chilled and frozen meals. The product mentioned herein is in particular not tested and therefore not validated for use in pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| UL File Number |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.905 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 | g/10 min | ASTM D1238, ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 99 | ASTM D785 | |
| Shore Hardness (Shore D) | 63 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| 1% Secant 1 | 1200 | MPa | ASTM D638 |
| -- | 1150 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield 2 | 29.0 | MPa | ASTM D638 |
| Yield | 28.0 | MPa | ISO 527-2/1A/50 |
| Tensile Elongation | |||
| Yield 3 | 12 | % | ASTM D638 |
| Yield | 12 | % | ISO 527-2/1A/50 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| 0°C | 5.0 | kJ/m² | |
| 23°C | 40 | kJ/m² | |
| Notched Izod Impact | |||
| 0°C | 50 | J/m | ASTM D256A |
| 23°C | 400 | J/m | ASTM D256A |
| 0°C | 4.5 | kJ/m² | ISO 180/1A |
| 23°C | 30 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed | 80.0 | °C | ASTM D648 |
| 0.45 MPa, Unannealed 4 | 75.0 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed | 55.0 | °C | ASTM D648 |
| 1.8 MPa, Unannealed 5 | 50.0 | °C | ISO 75-2/Af |
| Vicat Softening Temperature | |||
| -- | 140 | °C | ASTM D1525, ISO 306/A120 6 6 |
| -- | 75.0 | °C | ASTM D1525 7 |
| -- | 70.0 | °C | ISO 306/B120 |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze | 36 | % | ASTM D1003 |
| Note Message | |
|---|---|
| 1 . | 1.0 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | testbar 80*10*4mm |
| 5 . | testbar 80*10*4mm |
| 6 . | Rate B (120°C/h), Loading 1 (10 N) |
| 7 . | Rate B (120°C/h), Loading 2 (50 N) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| ACCUTECH鈩?HP0339C40L1 | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| DeWAL DW 402 | DeWAL Industries | UHMWPE | DeWAL |
| Hostaform® S 27064 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |
| POLIMAXX 2311SCXTA4 | IRPC Public Company Limited | PP Impact Copolymer | POLIMAXX |
| Sylvin 9077-95LMW White 1457 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |