ChronoFlex® C 80A
| Category: | PUR, Unspecified , Polyurethane |
| Manufacturer: | CardioTech International, Inc. |
| Trademark: | ChronoFlex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vRXvUN_ChronoFlex-C-80A.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
ChronoFlex®C 80A is a polyurethane material,. This product is available in North America and is processed by extrusion. ChronoFlex®The main characteristics of C 80A are: chemical resistance. ChronoFlex®The typical application areas of C 80A are: medical/health care |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (210°C/2.16 kg) | 8.0 | g/10 min | ASTM D1238 |
| Water Absorption (Equilibrium) | 1.2 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 80 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | ASTM D638 | ||
| 100% secant : 23°C | 6.96 | MPa | ASTM D638 |
| 300% secant : 23°C | 7.24 | MPa | ASTM D638 |
| Tensile Strength (Break, 23°C) | 41.4 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 450 | % | ASTM D638 |
| Flexural Modulus | 37.9 | MPa | ASTM D790 |
| Flexural Strength | 2.41 | MPa | ASTM D790 |
| Coefficient of Friction (vs. Itself - Dynamic) | 1.5 | ASTM D1894 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% strain | 5.34 | MPa | ASTM D412 |
| 300% strain | 4.14 | MPa | ASTM D412 |
| Tensile Strength (Yield) | 45.5 | MPa | ASTM D412 |
| Tensile Elongation (Yield) | 480 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 71.1 | °C | ASTM D1525 |
| Melting Temperature | 191 - 221 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength | 14 | kV/mm | ASTM D149 |
| Additional Information |
|---|
| Ultimate Tensile Strength, ASTM D638, 73 °F: 5500 to 6500 psiUltimate Tensile Strain, ASTM D638, 73 °F: 400 to 490 %100% Secant Modulus, ASTM D638, 73 °F: 770 to 1250 psi300% Secant Modulus, ASTM D638, 73 °F: 700 to 1400 psiAbrasion Resistance, ASTM D1044, 1000 cycles: 0.008%Recommended Sterilization Method, No standard: GammaClass VI Biocompactibility Test, USP XXII: Pass |
| Extrusion | Nominal Value | Unit | |
|---|---|---|---|
| Drying Time | 3.0 - 4.0 | hr | |
| Cylinder Zone 1 Temp. | 160 | °C | |
| Cylinder Zone 2 Temp. | 166 | °C | |
| Cylinder Zone 3 Temp. | 171 | °C | |
| Melt Temperature | 174 | °C | |
| Die Temperature | 174 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RJM SN501M30 | RJM International, Inc. | Nylon 6 | RJM |
| Ferro PP NPP00GC17NA | Ferro Corporation | PP Homopolymer | Ferro PP |
| Flexathene® TP4308HR | LyondellBasell Industries | Polyolefin, Unspecified | Flexathene® |
| Ebalta SG 130 / PUR 11 | Ebalta Kunststoff GmbH | PUR, Unspecified | Ebalta |
| Durethan® BKV 30 FN00 000000 | LANXESS Corporation | Nylon 6 | Durethan® |