Acudel® 22000
| Category: | PPSU, Modified , Modified Polyphenylsulfone |
| Manufacturer: | Solvay Specialty Polymers |
| Trademark: | Acudel® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vQuG43_Acudel-22000.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
Acudel 22000 is a high-temperature, high-performance modified polyphenyl sulfone resin composite material with very good hydrolysis stability, excellent acid and alkali resistance, and good stress cracking resistance in various chemical environments. In addition, Acudel 22000 resin has excellent toughness, although its crack resistance is slightly lower than that of Radel.®polyphenylsulfone, but better than Udel®Polysulfone and Veradel®Polyethersulfone. Overall, the performance of Acudel 22000 is between polysulfone and polyphenylsulfone. In addition to good mechanical and thermal properties, Acudel 22000 resins have excellent electrical properties and inherent flame retardancy over a wide temperature range. -natural color: Acudel 22000 NT15-black: Acudel 22000 BK937
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.28 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (380°C/2.16 kg) | 12 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.30 | % | ASTM D570 |
| Water absorption- (30 days) | 0.90 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2690 | MPa | ASTM D638 |
| Tensile Strength | 77.2 | MPa | ASTM D638 |
| Tensile Elongation | ASTM D638 | ||
| Yield | 6.7 | % | ASTM D638 |
| Fracture | 50 | % | ASTM D638 |
| Flexural Modulus | 2760 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 108 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 110 | J/m | ASTM D256 |
| Tensile Impact Strength | 368 | kJ/m² | ASTM D1822 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Annealed, 3.18 mm) | 197 | °C | ASTM D648 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | > 9.0E+15 | ohms·cm | ASTM D257 |
| Dielectric Strength (3.18 mm) | 19 | kV/mm | ASTM D149 |
| Dielectric Constant (1 MHz) | 3.40 | ASTM D150 | |
| Dissipation Factor (1 MHz) | 8.0E-3 | ASTM D150 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 177 | °C | |
| Drying Time | 2.5 | hr | |
| Processing (Melt) Temp | 360 - 391 | °C | |
| Mold Temperature | 138 - 163 | °C | |
| Injection Rate | Fast | ||
| Screw Compression Ratio | 2.2:1.0 |
| Injection instructions |
|---|
| 建议最低干燥要求为：350 °F （177°C ）温度下2.5小时，或300 ° F（149 °C）温度下4小时。 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARCOBLEND 1000 BK01 | POLY GIN | PC | MARCOBLEND |
| Zythane® 6065D | Alliance Polymers & Services | TPU-Polyether | Zythane® |
| NuSil CV2-2644 | NuSil Technology | Silicone | NuSil |
| INELEC PPASUZ 9MAX | Infinity LTL Engineered Compounds | PP, Unspecified | INELEC |
| Iupiace® VSG635V | Mitsubishi Engineering-Plastics Corp | PPE+PS | Iupiace® |