SABIC® PPcompound 7610
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® PPcompound |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vQWqfY_SABIC-PPcompound-7610.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® PPcompound 7610 is a mineral filled modified polypropylene. This material combines good flow with a good impact and high stiffness level. The material is UV stabilized and offers a good scratch resistance and a low shrinkage/CLTE. Typical applications include unpainted automotive exterior parts such as lateral siding, rocker panels and bumper strips. SABIC® PPcompound 7610 is a designated automotive grade. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.03 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 18 | g/10 min | ISO 1133 |
| Molding Shrinkage (24 hr) | 0.60 | % | Internal Method |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2/5/50 | ||
| Yield, 3.20 mm, Injection Molded | 18.0 | MPa | |
| Break, 3.20 mm, Injection Molded | 15.0 | MPa | |
| Tensile Strain (Break, 3.20 mm, Injection Molded) | > 400 | % | ISO 527-2/5/50 |
| Flexural Modulus 1(Injection Molded) | 1400 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C, Injection Molded) | No Break | ISO 179/1eA | |
| Charpy Unnotched Impact Strength (-40°C, Injection Molded) | No Break | ISO 179/1eU | |
| Notched Izod Impact Strength | ISO 180/4A | ||
| -20°C, Injection Molded | 10 | kJ/m² | |
| 0°C, Injection Molded | No Break | ||
| 23°C, Injection Molded | No Break |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (0.45 MPa, Unannealed) | 100 | °C | ISO 75-2/B |
| Vicat Softening Temperature | 120 | °C | ISO 306/A |
| CLTE - Flow | ASTM D696 | ||
| -30 to 30°C | 5.0E-5 | cm/cm/°C | |
| 23 to 80°C | 7.0E-5 | cm/cm/°C |
| Note Message | |
|---|---|
| 1 . | Method I (3 point load) |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RODRUN LC-5050GM | UNITIKA Plastics Division | LCP | RODRUN |
| Mirakutoran® TPU P22M | Japan Mirakutoran Inc. | TPU Alloy | Mirakutoran® TPU |
| Colorite 66 Series 7866 | Colorite Polymers | PVC, Unspecified | Colorite 66 Series |
| ESTOPLAST XU 425 HG36 | Ester Industries Ltd. | Nylon, Unspecified | ESTOPLAST XU |
| Ferro PP TPP20AF01HB YELLOW | Ferro Corporation | PP Homopolymer | Ferro PP |