SCHULAMID® XT 200 GF 35 BLACK 96.8001
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | A. Schulman Europe |
| Trademark: | SCHULAMID® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vQNmIK_SCHULAMIDXT200GF35BLACK968001.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| 35% glass fiber reinforced Polyamide 66 for high temperature applications |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Density | 1.42 | 1.42 | g/cm³ | ISO 1183/A |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 15000 | 8000 | MPa | ISO 527-2/1A/1 |
| Tensile Stress (Break) | 210 | 140 | MPa | ISO 527-2/1A/5 |
| Tensile Strain (Break) | 3.0 | 7.8 | % | ISO 527-2/1A/5 |
| Flexural Modulus | 12700 | -- | MPa | ISO 178 |
| Flexural Stress 1 | ISO 178 | |||
| 3.5% strain | 350 | -- | MPa | ISO 178 |
| 3.6% strain 2 | 350 | -- | MPa | ISO 178 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Charpy Notched Impact Strength | ||||
| -30°C | 10 | -- | kJ/m² | ISO 179/1eC |
| 23°C | 13 | 18 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | |||
| -30°C | 70 | -- | kJ/m² | ISO 179/1eU |
| 23°C | 90 kJ/m² | No Break | ISO 179/1eU |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Heat Deflection Temperature | ||||
| 0.45 MPa, not annealed | 237 | -- | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 212 | -- | °C | ISO 75-2/A |
| Additional Information |
|---|
| 干燥 1.) Not for use in food contact applications2.) Not for use in medical or pharmaceutical applications |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature | 80 | °C | |
| Drying Time | 3.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.040 - 0.10 | % | |
| Suggested Max Regrind | 10 | % | |
| Processing (Melt) Temp | 270 - 290 | °C | |
| Mold Temperature | 80 - 120 | °C |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| 2 . | at Break |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| TAROMID A 280 R2 | Taro Plast S.p.A. | Nylon 66 | TAROMID A |
| Ecodear® Prototype - High Flow | Toray Resin Company | PLA | Ecodear® |
| KRATON® G1750 M | Kraton Polymers LLC | EP | KRATON® |
| LEXAN™ CFR9712 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| Sylvin 9067-90 GREY 9166 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |