Infino WX-7010
| Category: | ASA+PC , Acrylonitrile Styrene Acrylate + PC |
| Manufacturer: | LOTTE ADVANCED MATERIALS CO., LTD. |
| Trademark: | Infino |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vQ9FSK_InfinoWX7010.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Infino WX-7010 is an acrylonitrile-styrene-acrylate PC (ASA PC) product,. It is available in North America, Africa and the Middle East, Latin America, Europe or Asia Pacific. Typical application areas are: automotive industry. The main characteristics are: good weather resistance. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity (Natural) | 1.16 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) (250°C/10.0 kg) | 30 | g/10 min | ASTM D1238, ISO 1133 |
| Molding Shrinkage | |||
| Flow : 3.20mm | 0.40 - 0.70 | % | ASTM D955 |
| Transverse flow : 3.20mm | 0.40 - 0.70 | % | ASTM D955 |
| Lateral flow : 3.20mm | 0.40 - 0.70 | % | ISO 2577 |
| Traffic : 3.20mm | 0.40 - 0.70 | % | ISO 2577 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness | |||
| Class r | 111 | ASTM D785 | |
| R scale | 110 | ISO 2039-2 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 1900 | MPa | ASTM D638 |
| -- | 1950 | MPa | ISO 527-2/50 |
| Tensile Strength | |||
| Yield 2 | 54.0 | MPa | ASTM D638 |
| Yield | 56.0 | MPa | ISO 527-2/50 |
| Fracture 3 | 49.0 | MPa | ASTM D638 |
| Fracture | 50.0 | MPa | ISO 527-2/50 |
| Tensile Elongation | |||
| Fracture 4 | 65 | % | ASTM D638 |
| Fracture | 66 | % | ISO 527-2/50 |
| Flexural Modulus | |||
| -- 5 | 2100 | MPa | ASTM D790 |
| -- 6 | 2250 | MPa | ISO 178 |
| Flexural Strength | |||
| -- 7 | 74.0 | MPa | ASTM D790 |
| -- 8 | 80.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength 9(23°C) | 60 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact | |||
| -30°C, 3.18 mm | 200 | J/m | ASTM D256 |
| -30°C, 6.35 mm | 150 | J/m | ASTM D256 |
| 23°C, 3.18 mm | 640 | J/m | ASTM D256 |
| 23°C, 6.35 mm | 440 | J/m | ASTM D256 |
| -30°C 10 | 19 | kJ/m² | ISO 180/1A |
| 23°C 11 | 50 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, unannealed, 6.40mm | 124 | °C | ASTM D648 |
| 0.45 MPa, unannealed, 4.00mm | 120 | °C | ISO 75-2/B |
| 1.8 MPa, unannealed, 6.40mm | 108 | °C | ASTM D648 |
| 1.8 MPa, not annealed, 4.00mm | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 120 | °C | ISO 306/B50 |
| Linear thermal expansion coefficient | ASTM E831, ISO 11359-2 | ||
| Flow : 40 to 100°C | 8.0E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Horizontal : 40 to 100°C | 8.5E-5 | cm/cm/°C | ASTM E831, ISO 11359-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | |||
| -- | 90 - 110 | °C | |
| Hot air dryer | 80 - 100 | °C | |
| Drying Time | |||
| -- | 2.0 - 4.0 | hr | |
| Hot air dryer | 2.0 - 4.0 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 210 - 230 | °C | |
| Middle Temperature | 230 - 250 | °C | |
| Front Temperature | 250 - 265 | °C | |
| Nozzle Temperature | 280 | °C | |
| Mold Temperature | 60 - 90 | °C | |
| Injection Pressure | 78.5 | MPa | |
| Back Pressure | 0.490 - 2.45 | MPa | |
| Screw Speed | 50 - 80 | rpm |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 50 mm/min |
| 4 . | 50 mm/min |
| 5 . | 2.8 mm/min |
| 6 . | 2.0 mm/min |
| 7 . | 2.8 mm/min |
| 8 . | 2.0 mm/min |
| 9 . | Thickness: 4mm |
| 10 . | Thickness: 4mm |
| 11 . | Thickness: 4mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Multi-Flam™ 0803 | Multibase, A Dow Corning Company | LDPE | Multi-Flam™ |
| Daplen™ EE158AIB | Borealis AG | TPO | Daplen™ |
| FHR EPS 55-6655 | Flint Hills Resources, LP | PS (EPS) | FHR EPS |
| EGYPTENE HD 5403 EA | Sidpec (Sidi Kerir Petrochemicals Co.) | HDPE | EGYPTENE |
| HAIPLEN H30 G3 | Taro Plast S.p.A. | PP Homopolymer | HAIPLEN |