HIPREN® EM 1502 T
| Category: | SBR, Emulsion , Emulsion Styrene Butadiene Rubber |
| Manufacturer: | HIP-PetroHemija |
| Trademark: | HIPREN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vOiNql_HIPREN-EM-1502-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
HIPREN® EM 1502 T is produced by cold copolymerisation process, with the use of rosin and fatty acids soaps as emulsifiers, and contains 23.5% styrene bounded in polymer. The rubber is stabilised with non-staining antioxidant. HIPREN® EM 1502 T is light coloured, without nitrosoamine. HIPREN® EM 1502 T is compatible with natural rubber and other synthetic rubbers. Good compatibility, easy incorporation of various compounding ingredients provide possibility of mixing formulations for different applications requirement. Application: HIPREN EM 1502 T is used for production of light coloured compounds and products requiring high transparency including light coloured wheel sides, sport goods, flooring, medical and house hold articles. HIPREN® EM 1502 T has Health Certificate issued by Institute for Health Protection of Serbia |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Mooney Viscosity (ML 1+4, 100°C) | 51 | MU | ISO 289 |
| Bound Styrene | 23.5 | % | ISO 2453 |
| Ash Content | 0.4 | wt% | ISO 247 |
| Organic Acid | 6.0 | wt% | ISO 7781 |
| Soap | 0.5 | wt% | ISO 7781 |
| Stabilizer | 0.1 to 1.0 | wt% | Internal Method |
| Volatile Matter | 0.50 | wt% | ISO 248 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time | ISO 6502 | ||
| 50% | 6.5 to 10.5 | min | |
| 90% | 12.5 to 17.5 | min | |
| Scorch Time | 2.5 to 4.5 | min | ISO 6502 |
| Torque | ISO 6502 | ||
| Max | 20.5 to 24.5 | dNm | |
| Min | 2.00 to 3.00 | dNm |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness 1(Shore A) | 66 to 74 | ISO 868 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress 2(300% Strain, 145°C) | 14.4 to 19.4 | MPa | ISO 37 |
| Tensile Stress 3(Break, 145°C) | > 22.0 | MPa | ISO 37 |
| Tensile Elongation 4(Break, 145°C) | > 350 | % | ISO 37 |
| Bayshore Resilience 5 | > 40 | % | ISO 4662 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 91.5 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| 2 . | Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| 3 . | Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| 4 . | Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| 5 . | Vulcanization temperature 145°C; Vulcanization time 35 min; Test specimen SI |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| NORYL™ HM3020H resin | SABIC Innovative Plastics Asia Pacific | PPE+PS | NORYL™ |
| Electrafil® NY-7/EC NAT | Techmer Engineered Solutions | Nylon 6 | Electrafil® |
| EPO-TEK® H20E-MP | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| HIVOREX 5100ST | Lotte Chemical Corporation | HDPE | HIVOREX |
| LNP™ THERMOCOMP™ ZF006 compound | SABIC Innovative Plastics | PPE+PS | LNP™ THERMOCOMP™ |