Plexar® PX2600
| Category: | PE, Unspecified , Polyethylene |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Plexar® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vOUNPy_PlexarPX2600.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Plexar tie-layers are chemically modified resins used to bond unlike materials, primarily in packaging and industrial applications. Common adherents include polyethylene resins and copolymers, EVA, EMA, polypropylene, polyamide (nylon), ethylene vinyl alcohol copolymers (EVOH), ionomer and other sealants, polyethylene terephthalate (PET) resins and copolymers, styrenic polymers, metal, and paperboard. Product grades primarily used for blown and cast films, sheet and thermoforming, blow molding, extrusion coating and lamination, tubing, pipe, and other specialty applications are available in pellet form. Contact your Plexar sales and/or Equistar technical service representative for more information and specific recommendations for your application(s). |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 0.927 | g/cm³ | ASTM D1505 |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 6.0 | g/10 min | ASTM D1238 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 99.0 | °C | ASTM D1525 |
| Note Message | |
|---|---|
| 1 . | 23°C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Quadrant EPP Delrin® AF Blend | Quadrant Engineering Plastic Products | Acetal (POM) Homopolymer | Quadrant EPP |
| Minlon® EFE6053 BK413 | DuPont Performance Polymers | Nylon 66 | Minlon® |
| TOTAL Polyethylene HDPE D4720 | TOTAL Refining & Chemicals | HDPE, MMW | TOTAL Polyethylene |
| Badamid® LA70 GF25 HH | Bada AG | Nylon 66 | Badamid® |
| Kostil® B 266 | Versalis S.p.A. | SAN | Kostil® |