Durolon® G2510
| Category: | PC , Polycarbonate |
| Manufacturer: | Unigel Plásticos |
| Trademark: | Durolon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vNi3Bz_Durolon-G2510.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Injection molding, natural polycarbonate 10% glass fiber reinforced. Enhanced tensile strength, dimensional stability, hardness and heat distortion resistance performance. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.27 | g/cm³ | ASTM D792, ISO 1183 |
| Molding Shrinkage - Flow | 0.50 - 0.60 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (M-Scale) | 90 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3900 | MPa | ASTM D638, ISO 527-2 |
| Tensile Strength | ASTM D638, ISO 527-2 | ||
| Yield | 88.0 | MPa | ASTM D638, ISO 527-2 |
| Fracture | 83.0 | MPa | ASTM D638, ISO 527-2 |
| Tensile Elongation (Break) | 5.0 | % | ASTM D638, ISO 527-2 |
| Flexural Modulus | 3920 | MPa | ASTM D790, ISO 178 |
| Flexural Strength | 120 | MPa | ASTM D790, ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (3.20 mm) | 98 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 136 | °C | ASTM D648, ISO 75-2/A |
| CLTE - Flow | 4.5E-5 | cm/cm/°C | ASTM D696 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+16 | ohms·cm | ASTM D257 |
| Dielectric Strength (1.60 mm) | 22 | kV/mm | ASTM D149 |
| Dielectric Constant | ASTM D150 | ||
| 60 Hz | 3.10 | ASTM D150 | |
| 1 MHz | 2.95 | ASTM D150 | |
| Dissipation Factor | ASTM D150 | ||
| 60 Hz | 8.0E-4 | ASTM D150 | |
| 1 MHz | 9.0E-3 | ASTM D150 | |
| Arc Resistance | 110 | sec | ASTM D495 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Glow Wire Ignition Temperature (3.20 mm) | 960 | °C | IEC 60695-2-13 |
| Additional Information |
|---|
| Volume Resistivity, ASTM D257: >1E16 ohm-cmDielectric Strength, ASTM D149, 1.6 mm: >22 kV/mm |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 4.0 | hr | |
| Rear Temperature | 270 | °C | |
| Middle Temperature | 280 | °C | |
| Front Temperature | 290 | °C | |
| Nozzle Temperature | 280 | °C | |
| Processing (Melt) Temp | 240 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moharamplast LLDPE MP50035U | Moharamplast S.A.E | LLDPE | Moharamplast LLDPE |
| DOW™ HDPE LP 8000 | The Dow Chemical Company | HDPE | DOW™ HDPE |
| AFLAS® 300S | Asahi Glass Co., Ltd. | Fluorelastomer | AFLAS® |
| Sylvin 4299-60 Natural | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| Sylvin 9993-85 Brown 7458 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |