Skyrol® SH96D
| Category: | PET , Polyethylene Terephthalate |
| Manufacturer: | SKC Inc. |
| Trademark: | Skyrol® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vNVuaQ_Skyrol-SH96D.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Skyrol® SH96D is an optically clear and anti-static pretreated polyester film. SH96D is primarily used as substrates for microfilm, overhead projector film and laminating film, since its anti-static property can be retained after several uses and is seldom influenced by humidity. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density 1 | 1.40 | g/cm³ | ASTM D1505 |
| Molding Shrinkage | Internal Method | ||
| Flow : 150°C, 30 min, 0.0860 mm | 1.5 | % | |
| Flow : 150°C, 30 min, 0.107 mm | 1.5 | % | |
| Across Flow : 150°C, 30 min, 0.0860 mm | 1.0 | % | |
| Across Flow : 150°C, 30 min, 0.107 mm | 0.90 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic 2 | 0.30 | ||
| vs. Itself - Dynamic 3 | 0.30 | ||
| vs. Itself - Static 4 | 0.30 | ||
| vs. Itself - Static 5 | 0.30 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | ASTM D882 | ||
| MD : Yield, 86 µm | 214 | MPa | |
| MD : Yield, 110 µm | 200 | MPa | |
| TD : Yield, 86 µm | 234 | MPa | |
| TD : Yield, 110 µm | 228 | MPa | |
| Tensile Elongation | ASTM D882 | ||
| MD : Break, 86 µm | 150 | % | |
| MD : Break, 110 µm | 160 | % | |
| TD : Break, 86 µm | 110 | % | |
| TD : Break, 110 µm | 110 | % |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Gardner Gloss | ASTM D523 | ||
| 86.0 µm | 174 | ||
| 107 µm | 173 | ||
| Transmittance | ASTM D1003 | ||
| 86.0 µm | 89.0 | % | |
| 107 µm | 89.0 | % | |
| Haze | ASTM D1003 | ||
| 86.0 µm | 3.2 | % | |
| 107 µm | 4.0 | % |
| Note Message | |
|---|---|
| 1 . | 107.4 µm |
| 2 . | 107.4 µm |
| 3 . | 86 µm |
| 4 . | 86 µm |
| 5 . | 107.4 µm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 209 UV | RTP Company | Nylon 66 | RTP |
| RABALON® SJ7400 | Mitsubishi Chemical Performance Polymers, Inc. | TPE | RABALON® |
| GAPEX® RPP20EC10NA | Ferro Corporation | PP Homopolymer | GAPEX® |
| KOPA® KN333HI4 | Kolon Plastics, Inc. | Nylon 66 | KOPA® |
| KumhoSunny PC HCG2530MP | Shanghai KumhoSunny Plastics Co., Ltd. | PC | KumhoSunny PC |