Quadrant EPP TIVAR® Dockguard Uniblend
| Category: | UHMWPE , Ultra High Molecular Weight Polyethylene |
| Manufacturer: | Quadrant Engineering Plastic Products |
| Trademark: | Quadrant EPP |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vN4qaL_Quadrant-EPP-TIVAR-Dockguard-Uniblend.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Quadrant EPP TIVAR® Dockguard Uniblend is an Ultra High Molecular Weight Polyethylene product. It is available in North America. Characteristics include:
|
| General Information | |
|---|---|
| Recycled Content |
|
| Features |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.940 | g/cm³ | ASTM D792 |
| Water Absorption | ASTM D570 | ||
| 24 hr | < 0.010 | % | |
| Saturation | < 0.010 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 68 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 800 | MPa | ASTM D638 |
| Tensile Strength (Ultimate) | 37.9 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 250 | % | ASTM D638 |
| Flexural Modulus | 800 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 24.8 | MPa | ASTM D790 |
| Compressive Modulus | 689 | MPa | ASTM D695 |
| Compressive Strength (10% Strain, 23°C) | 22.8 | MPa | ASTM D695 |
| Coefficient of Friction | 0.15 | ASTM D1894 | |
| Abrasion 1 | 13 | ASTM D4020 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Maximum Use Temperature - Long Term, Air | 82 | °C |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Limiting Pressure Velocity 2 | 0.0701 | MPa·m/s | Internal Method |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | No Break | ASTM D256A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 46.7 | °C | ASTM D648 |
| Peak Crystallization Temperature (DSC) | 127 | °C | ASTM D3418 |
| CLTE - Flow 3(-40 to 149°C) | 1.6E-4 | cm/cm/°C | ASTM E831 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | ASTM D257 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating (3.18 mm, Estimated Rating) | HB | UL 94 |
| Note Message | |
|---|---|
| 1 . | Sand Slurry; 1018 Steel = 100 |
| 2 . | 4:1 safety factor |
| 3 . | 68°F |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Supol HT345E | LyondellBasell Industries | PP Copolymer | Supol |
| Ultramid® 1503-2 NF2004 | BASF Corporation | Nylon 66 | Ultramid® |
| UMG ALLOY® TA-820CA | UMG ABS, Ltd. | ASA+PC | UMG ALLOY® |
| ASI POLYPROPYLENE 3495 | A. Schulman Inc. | PP Impact Copolymer | ASI POLYPROPYLENE |
| Sylvin 5175-92 Red 6243 | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |