POLYNIL® P43/4
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Nilit Plastics |
| Trademark: | POLYNIL® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vMiDYz_POLYNILP434.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
PA 6.6 RESIN
2.6 VISCOSITY, FDA COMPLIANT, MOISTURE <0.4% |
| General Information | |
|---|---|
| Uses |
|
| Agency Ratings |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.14 | g/cm³ | ISO 1183 |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.5 | % | ISO 62 |
| Saturated, 23°C | 8.5 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3100 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 81.0 | MPa | ISO 527-2 |
| Tensile Strain (Break, 23°C) | 50 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2850 | MPa | ISO 178 |
| Flexural Stress (23°C) | 120 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 4.5 | kJ/m² | ISO 179/1eA |
| 23°C | 5.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU | |
| Notched Izod Impact | ISO 180/A | ||
| -30°C | 4.5 | kJ/m² | ISO 180/A |
| 23°C | 5.5 | kJ/m² | ISO 180/A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 225 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 72.0 | °C | ISO 75-2/A |
| Continuous Use Temperature 1 | 85.0 | °C | IEC 60216 |
| Vicat Softening Temperature | 240 | °C | ISO 306/B |
| Ball Pressure Test | IEC 60695-10-2 | ||
| 125°C | Pass | IEC 60695-10-2 | |
| 165°C | Pass | IEC 60695-10-2 | |
| Melting Temperature | 258 | °C |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Dielectric Strength (2.00 mm) | 18 | kV/mm | IEC 60243-1 |
| Comparative Tracking Index (3.20 mm, Solution A) | 600 | V | IEC 60112 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.8 mm | V-2 | UL 94 | |
| 3.2 mm | V-2 | UL 94 | |
| Glow Wire Flammability Index | IEC 60695-2-12 | ||
| 0.8 mm | 750 | °C | IEC 60695-2-12 |
| 3.2 mm | 850 | °C | IEC 60695-2-12 |
| Glow Wire Ignition Temperature | IEC 60695-2-13 | ||
| 0.8 mm | 775 | °C | IEC 60695-2-13 |
| 3.2 mm | 750 | °C | IEC 60695-2-13 |
| Oxygen Index | 28 | % | ISO 4589-2 |
| Note Message | |
|---|---|
| 1 . | 20000 hr |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Ravago Compounds HMP-307 (Roto) | Ravago Manufacturing Americas, LLC | MDPE | Ravago Compounds |
| Supol HT144HE | LyondellBasell Industries | PP Copolymer | Supol |
| Nipol® 1043 | Zeon Chemicals L.P. | NBR | Nipol® |
| Bergamid™ B70 G15 U NC034 | PolyOne Corporation | Nylon 6 | Bergamid™ |
| Jiangsu Sinarise EX8535X | Jiangsu Sinarise New Material Technology Co., Ltd | TPE | Jiangsu Sinarise |