TORZEN® U4640NL NC01
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vMAXdX_TORZEN-U4640NL-NC01.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN® U4640NL NC01 is a highly nucleated, lubricated PA66 resin suitable for injection molding, where fast crystallization and fast cycle times are required. It is lubricated internally and externally for excellent machine feed and mold release. U4640NL is also available in black. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.14 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 1.0 | % | |
| Flow : 2.00 mm | 1.0 | % | |
| Water Absorption (23°C, 24 hr) | 1.6 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3400 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 92.0 | MPa | ISO 527-2/50 |
| Tensile Strain | ISO 527-2 | ||
| Yield | 4.2 | % | |
| Break | 16 | % | |
| Flexural Modulus | 3300 | MPa | ISO 178 |
| Flexural Stress | 105 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -30°C | 2.3 | kJ/m² | |
| 23°C | 3.0 | kJ/m² | |
| Charpy Unnotched Impact Strength | ISO 179 | ||
| -30°C | No Break | ||
| 23°C | No Break | ||
| Notched Izod Impact Strength (23°C) | 3.5 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 263 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Screw Speed | 75 to 180 | rpm | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 1300 TFE 20 | RTP Company | PPS | RTP |
| Nipol® NBR N1201L | Zeon Corporation | NBR | Nipol® NBR |
| Elastron® G G300.A50.B | Elastron USA, Inc. | SEBS | Elastron® G |
| Globalene® PT262 | Lee Chang Yung Chemical Industry Corp. | PP Alloy | Globalene® |
| OmniCarb™ PC/PBT 400 | OMNI Plastics, LLC | PC+PBT | OmniCarb™ |