TORZEN Marathon™ G3500XHL BK20
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | INVISTA Engineering Polymers |
| Trademark: | TORZEN Marathon™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vM7SWh_TORZEN-Marathon-G3500XHL-BK20.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| TORZEN Marathon™ G3500XHL BK20 is a 35% glass reinforced, heat stabilized, black, PA66 resin with a significantly improved balance of continuous heat and peak temperature property retention, along with higher flow and similar shrinkage compared to conventional PA66 resins |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.42 | g/cm³ | ISO 1183 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow : 2.00 mm | 0.90 to 1.1 | % | |
| Flow : 2.00 mm | 0.25 to 0.35 | % | |
| Water Absorption | ISO 62 | ||
| 23°C, 24 hr | 1.1 | % | |
| Equilibrium, 23°C, 50% RH | 1.7 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 11500 | MPa | ISO 527-2 |
| Tensile Stress (Break) | 210 | MPa | ISO 527-2 |
| Tensile Strain (Break) | 3.0 | % | ISO 527-2 |
| Flexural Modulus | 10500 | MPa | ISO 178 |
| Flexural Stress | 320 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179 | ||
| -40°C | 10 | kJ/m² | |
| 23°C | 12 | kJ/m² | |
| Notched Izod Impact Strength (23°C) | 12 | kJ/m² | ISO 180 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 260 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 250 | °C | ISO 75-2/A |
| Melting Temperature | 262 | °C | ISO 11357-3 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Suggested Max Moisture | 0.080 to 0.18 | % | |
| Rear Temperature | 250 to 270 | °C | |
| Middle Temperature | 270 to 290 | °C | |
| Front Temperature | 270 to 290 | °C | |
| Nozzle Temperature | 270 to 290 | °C | |
| Processing (Melt) Temp | 280 to 300 | °C | |
| Mold Temperature | 50.0 to 90.0 | °C | |
| Back Pressure | 0.200 to 1.00 | MPa | |
| Cushion | 4.00 to 6.00 | mm | |
| Vent Depth | 7.0E-3 to 0.040 | mm | |
| Screw Speed | Low rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MonoSol® M7061 | MonoSol, LLC | PVOH | MonoSol® |
| Fainplast PVC RI 50 | Fainplast Compounds S.r.l | PVC, Rigid | Fainplast PVC |
| HiFill® PA6 0445 A | Techmer Engineered Solutions | Nylon 6 | HiFill® |
| LNP™ THERMOCOMP™ DX07408 compound | SABIC Innovative Plastics | PC | LNP™ THERMOCOMP™ |
| PETILEN H2-26T | PETKIM Petrokimya Holding A.S. | LDPE | PETILEN |