E-RIALFILL C 15 20 T
| Category: | PP Copolymer , Polypropylene Copolymer |
| Manufacturer: | RIALTI Srl |
| Trademark: | E-RIALFILL |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vLwPhU_E-RIALFILL-C-15-20-T.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Polypropylene compound obtained by complete recycling of industrial scrap, 20%filled with talc. Flowability, for injection molding of big dimension articles, good impact strength and good stiffness. Available just in black version. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | ISO 294-4 | ||
| Across Flow | 1.4 | % | |
| Flow | 1.4 | % | |
| Water Absorption 1(23°C, 24 hr) | 0.020 | % | ISO 62 |
| Ash Content | 20 | % | ISO 3451 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Shore Hardness (Shore D, 15 sec) | 68 | ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 1950 | MPa | ISO 527-2/2 |
| Tensile Stress | ISO 527-2/20 | ||
| Yield, 23°C | 21.0 | MPa | |
| Break, 23°C | 16.0 | MPa | |
| Tensile Strain | ISO 527-2/20 | ||
| Yield, 23°C | 7.0 | % | |
| Break, 23°C | 120 | % | |
| Flexural Modulus 2(23°C) | 1700 | MPa | ISO 178 |
| Flexural Stress (23°C) | 30.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | ISO 179/1eA | ||
| -30°C | 2.2 | kJ/m² | |
| 23°C | 6.8 | kJ/m² | |
| Charpy Unnotched Impact Strength (23°C) | 50 | kJ/m² | ISO 179/1eU |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -40°C | 2.3 | kJ/m² | |
| -30°C | 2.5 | kJ/m² | |
| -20°C | 2.7 | kJ/m² | |
| 23°C | 6.0 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 96.0 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 56.0 | °C | ISO 75-2/A |
| Vicat Softening Temperature | |||
| -- | 130 | °C | ISO 306/A50 |
| -- | 68.0 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating (1.50 mm) | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 to 90.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 180 to 200 | °C | |
| Mold Temperature | 30.0 to 50.0 | °C |
| Note Message | |
|---|---|
| 1 . | 50%RH |
| 2 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Taitarex® 861N / B / W | Taita Chemical Company, Ltd. | PS (GPPS) | Taitarex® |
| GLS 422-126 | PolyOne Corporation | TPE | GLS |
| Hostalen PP H2222 36 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| KEBAFLEX® SG 85 A.1 | BARLOG plastics GmbH | TES | KEBAFLEX® |
| SABIC® PC PC1800R resin | SABIC Innovative Plastics Asia Pacific | PC | SABIC® PC |