Celcon® UV270Z
| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Celanese Corporation |
| Trademark: | Celcon® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vL1S6K_Celcon-UV270Z.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Celcon® UV270Z is a nominal 27 melt flow rate acetal copolymer which has been specially stabilized to prevent discoloration and deterioration of mechanical properties from ultraviolet light exposure. Celcon® UV270Z flow is designed to fill small and difficult to process parts such as speaker grills and other interior automotive parts. The material is available in precolored black or colors. |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| RoHS Compliance |
|
| Appearance |
|
| Multi-Point Data |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.41 | g/cm³ | ASTM D792, ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 27 | g/10 min | ASTM D1238 |
| Melt Volume-Flow Rate (MVR) (190°C/2.16 kg) | 23.0 | cm³/10min | ISO 1133 |
| Molding Shrinkage | |||
| Flow | 2.2 | % | ASTM D955 |
| Transverse flow | 1.8 | % | ASTM D955 |
| Vertical flow direction | 1.6 | % | ISO 294-4 |
| Flow direction | 1.7 | % | ISO 294-4 |
| Water Absorption | ISO 62 | ||
| Saturated, 23°C | 0.75 | % | ISO 62 |
| Equilibrium, 23°C, 50% RH | 0.20 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2700 | MPa | ISO 527-2/1A/1 |
| Tensile Strength | |||
| Yield, 23°C | 60.7 | MPa | ASTM D638 |
| Yield | 64.0 | MPa | ISO 527-2/1A/50 |
| Tensile Strain (Yield) | 8.0 | % | ISO 527-2/1A/50 |
| Flexural Modulus (23°C) | 2760 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 4.7 | kJ/m² | ISO 179/1eA |
| Notched Izod Impact (23°C) | 5.1 | kJ/m² | ISO 180/1A |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 1.8 MPa, not annealed | 110 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 90.0 | °C | ISO 75-2/A |
| Melting Temperature | |||
| -- 1 | 167 | °C | ISO 11357-3 |
| -- | 165 | °C | ASTM D3418 |
| Linear thermal expansion coefficient | ISO 11359-2 | ||
| Flow | 1.1E-4 | cm/cm/°C | ISO 11359-2 |
| Lateral | 1.2E-4 | cm/cm/°C | ISO 11359-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Volume Resistivity | 1.0E+14 | ohms·cm | ASTM D257 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 3.0 | hr | |
| Rear Temperature | 170 - 180 | °C | |
| Middle Temperature | 180 - 190 | °C | |
| Front Temperature | 180 - 190 | °C | |
| Nozzle Temperature | 190 - 200 | °C | |
| Processing (Melt) Temp | 180 - 200 | °C | |
| Mold Temperature | 80.0 - 120 | °C | |
| Injection Pressure | 60.0 - 120 | MPa | |
| Injection Rate | Slow-Moderate | ||
| Holding Pressure | 60.0 - 120 | MPa | |
| Back Pressure | 0.00 - 0.500 | MPa |
| Injection instructions |
|---|
| Manifold Temperature: 180 to 200°CZone 4 Temperature: 190 to 200°C |
| Note Message | |
|---|---|
| 1 . | 10°C/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Starex SF-0950 | SAMSUNG SDI CO., LTD. | MABS | Starex |
| GAPEX® HP RPP30EV05HB | Ferro Corporation | PP, Unspecified | GAPEX® HP |
| ELASTOSIL® LR 3066/70 A/B | Wacker Chemie AG | Silicone | ELASTOSIL® LR |
| EPO-TEK® OD2003 | Epoxy Technology Inc. | Epoxy | EPO-TEK® |
| LNP™ THERMOCOMP™ 9X11427 compound | SABIC Innovative Plastics | TP, Unspecified | LNP™ THERMOCOMP™ |