QR Resin QR-1015
| Category: | PC , Polycarbonate |
| Manufacturer: | QTR, Inc. |
| Trademark: | QR Resin |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vKvlHK_QR-Resin-QR-1015.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Available with UV (V) or Release (R). |
| General Information | |
|---|---|
| Features |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 15 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.60 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield) | 62.1 | MPa | ASTM D638 |
| Flexural Modulus | 2280 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 89.6 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 640 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 135 | °C | |
| 1.8 MPa, Unannealed | 127 | °C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 to 8.0 | hr | |
| Drying Time, Maximum | 8.0 | hr | |
| Rear Temperature | 254 to 277 | °C | |
| Middle Temperature | 266 to 299 | °C | |
| Front Temperature | 277 to 299 | °C | |
| Nozzle Temperature | 271 to 293 | °C | |
| Processing (Melt) Temp | 271 to 293 | °C | |
| Mold Temperature | 71.1 to 93.3 | °C |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Sylvin 2910-88 Clear | Sylvin Technologies Incorporated | PVC, Unspecified | Sylvin |
| TARFLON™ GZ2520 | Idemitsu Kosan Co., Ltd. | PC | TARFLON™ |
| Eltex® MMPE3940/10 | INEOS Olefins & Polymers Europe | HDPE | Eltex® |
| Hostacom G2 N02 100000 | LyondellBasell Industries | PP Homopolymer | Hostacom |
| LEXAN™ 3412HF resin | SABIC Innovative Plastics | PC | LEXAN™ |