SABIC® LDPE 2500N0
| Category: | LDPE , Low Density Polyethylene |
| Manufacturer: | Saudi Basic Industries Corporation (SABIC) |
| Trademark: | SABIC® LDPE |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vKv7Ow_SABIC-LDPE-2500N0.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
SABIC® LDPE 2500N0 is a grade without additives with very good shrink properties, stiffness and good bundle force. The grade has a good draw down ability. Application SABIC® LDPE 2500TN00 is typically used for application in shrinkhoods, industrial sacks, heavy duty bags and liners. This product is not intended for and must not be used in any pharmaceutical/medical applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 0.925 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (190°C/2.16 kg) | 0.40 | g/10 min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Coefficient of Friction (Blown Film) | 0.90 | ASTM D1894 |
| Films | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film Thickness - Tested | 50 | µm | |
| Tensile Modulus | ISO 527-3 | ||
| MD : 50 µm, blown film | 210 | MPa | ISO 527-3 |
| TD : 50 µm, blown film | 210 | MPa | ISO 527-3 |
| Tensile Stress | ISO 527-3 | ||
| MD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| TD : Yield, 50 µm, blown film | 12.0 | MPa | ISO 527-3 |
| MD : Broken, 50 µm, blown film | 27.0 | MPa | ISO 527-3 |
| TD : Broken, 50 µm, blown film | 23.0 | MPa | ISO 527-3 |
| Tensile Elongation | ISO 527-3 | ||
| MD : Broken, 50 µm, blown film | > 200 | % | ISO 527-3 |
| TD : Broken, 50 µm, blown film | > 500 | % | ISO 527-3 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Impact Strength - Blown Film (50.0 µm) | 200 | J/cm | ASTM D4272 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Blocking (50.0 µm) 1 | 20 | g | Internal method |
| Re-blocking (50.0 µm) 2 | g | Internal method | |
| Tear Strength 3 | ISO 6383-2 | ||
| MD : 50.0 µm | 35.0 | kN/m | ISO 6383-2 |
| TD : 50.0 µm | 40.0 | kN/m | ISO 6383-2 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Vicat Softening Temperature | 98.0 | °C | ISO 306/A |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Haze (50.0 µm, Blown Film) | 11 | % | ASTM D1003A |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Film properties have been measured at film of 50 µm with a BUR of 3.The film has been produced on Kiefel IBC blown film line with 200 kg/h. Die size 200 mm, die gap 0.8 mm. |
| Note Message | |
|---|---|
| 1 . | Blown Film |
| 2 . | Blown Film |
| 3 . | Blown Film |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Radilon® S RCP3010LK 322 NER | Radici Plastics | Nylon 6 | Radilon® |
| Epolene® C-17P | Westlake Chemical Corporation | LDPE | Epolene® |
| Laramid G/30 | LATI S.p.A. | PPA | Laramid |
| Karina IVORY PVC COMPOUND -E 655-35/1-F-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LNP™ STAT-KON™ FX91304 compound | SABIC Innovative Plastics | PE, Unspecified | LNP™ STAT-KON™ |