SABIC® LDPE 2102TN32 Datasheet,LDPE,Saudi Basic Industries Corporation (SABIC)-SHANGHAI SUSHENG

Message
SABIC® LDPE 2102TN32 is a general purpose grade with a high level of anti block and slip agent (E=erucamide). This grade offers good optical properties and an excellent draw down ability. SABIC® LDPE 2102TN32 is suitable for packaging films for food and industrial goods and for lamination films. This grade is especially suitable when ultimate down gauging is required. The usual melt-2 film thickness can be reduced by 10-40%, maintaining an adequate CoF level.

General Information
Additive	Anti-caking agent (800 ppm) Sliding agent (600 ppm)
Features	High smoothness High caking resistance Optical Foamable property Good stripping General
Uses	Packaging Films Laminate Industrial application Foam Food packaging
Forms	Particle
Processing Method	Blow film

Physical	Nominal Value	Unit	Test Method
Density	0.921	g/cm³	ISO 1183/A
Melt Mass-Flow Rate (MFR) (190°C/2.16 kg)	2.5	g/10 min	ISO 1133

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D, Compression Molded)	45		ISO 868

Mechanical	Nominal Value	Unit	Test Method
Coefficient of Friction (Blown Film)	0.20		ASTM D1894

Films	Nominal Value	Unit	Test Method
Tensile Modulus			ISO 527-3
MD : 25 µm, blown film	190	MPa	ISO 527-3
TD : 25 µm, blown film	190	MPa	ISO 527-3
Tensile Stress			ISO 527-3
MD : Yield, 25 µm, blown film	13.0	MPa	ISO 527-3
TD : Yield, 25 µm, blown film	11.0	MPa	ISO 527-3
MD : 25 µm, blown film	30.0	MPa	ISO 527-3
TD : 25 µm, blown film	18.0	MPa	ISO 527-3
Tensile Elongation			ISO 527-3
MD : Broken, 25 µm, blown film	> 100	%	ISO 527-3
TD : Broken, 25 µm, blown film	> 500	%	ISO 527-3

Thermal	Nominal Value	Unit	Test Method
Vicat Softening Temperature	90.0	°C	ISO 306/A50

Optical	Nominal Value	Unit	Test Method
Haze (25.0 µm, Blown Film)	12	%	ASTM D1003

Additional Information
25µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm.Modulus of Elasticity, SABIC Method: 250 MPaMelting Point, SABIC Method, DSC: 108°CCrystallization Temperature, SABIC Method, DSC: 96°CAverage Heat of Fusion, SABIC Method, DSC: 108 J/gClarity, SABIC Method, Blown Film, 25µm: 30mVBlocking, SABIC Method, Blown Film: <5gRe-blocking, SABIC Method, Blown Film: 10gImpact Strength, ASTM D4272, 25µm, Blown Film: 20 kJ/mTear Strength, ISO 6383-2, 25µm, Blown Film, TD: 20 kN/mTear Strength, ISO 6383-2, 25µm, Blown Film, MD: 50 kN/m

Additional Information

25µm blown film processed with a blow up ratio of 3:1 and a die gap of 0.8 mm.Modulus of Elasticity, SABIC Method: 250 MPaMelting Point, SABIC Method, DSC: 108°CCrystallization Temperature, SABIC Method, DSC: 96°CAverage Heat of Fusion, SABIC Method, DSC: 108 J/gClarity, SABIC Method, Blown Film, 25µm: 30mVBlocking, SABIC Method, Blown Film: <5gRe-blocking, SABIC Method, Blown Film: 10gImpact Strength, ASTM D4272, 25µm, Blown Film: 20 kJ/mTear Strength, ISO 6383-2, 25µm, Blown Film, TD: 20 kN/mTear Strength, ISO 6383-2, 25µm, Blown Film, MD: 50 kN/m

Category:	LDPE , Low Density Polyethylene
Manufacturer:	Saudi Basic Industries Corporation (SABIC)
Trademark:	SABIC® LDPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vKIKTM_SABIC-LDPE-2102TN32.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Ferro PP TPP20AR10BK	Ferro Corporation	PP, Unspecified	Ferro PP
Flextuff® S2801-00-E	Noble Polymers	TPE	Flextuff®
Paracril® CV80	INSA	NBR	Paracril®
Sylvin 8356-73 Brown 7437	Sylvin Technologies Incorporated	PVC, Unspecified	Sylvin
POCAN® T 7391 POS151 900044	LANXESS GmbH	PBT+PET	POCAN®