EpoxAmite® 101 FAST
| Category: | Epoxy , Epoxy; Epoxide |
| Manufacturer: | Smooth-On, Inc |
| Trademark: | EpoxAmite® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vIvN6y_EpoxAmite-101-FAST.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EpoxAmite® 100 Epoxy Laminating System is an easy-to-use liquid epoxy system formulated for a wide variety of fabrication applications. EpoxAmite® 100 Laminating System is unfilled, low in viscosity, odorless and cures at room temperature. Cured epoxy displays exceptional physical and performance properties. It can be sanded, shaped, machined, drilled, tapped and painted. EpoxAmite® 100 Laminating System can be used with reinforcements such as S-Glass, E-Glass, Kevlar and Carbon fibers for lay-up applications or composite parts. EpoxAmite® 100 Resin can also be mixed with fillers such as fumed silica for gel coat applications. Urefil® 3, Urefil® 7 and other fillers can be added for fairing, filleting or bonding applications. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D1475 |
| Specific Volume | 0.885 | cm³/g | ASTM D792 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Work Time - Thin Film | 30.0 | min |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Cure Time 1 | 6.0 to 8.0 | hr |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore D) | 84 | ASTM D2240 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 3070 | MPa | ASTM D638 |
| Tensile Strength | ASTM D638 | ||
| Break 2 | 242 | MPa | |
| Break | 54.7 | MPa | |
| Tensile Elongation (Break) | 2.5 | % | ASTM D638 |
| Flexural Modulus | 3230 | MPa | ASTM D790 |
| Flexural Strength | ASTM D790 | ||
| -- | 94.2 | MPa | |
| -- 3 | 212 | MPa | |
| Compressive Modulus | 837 | MPa | ASTM D695 |
| Compressive Strength | 79.6 | MPa | ASTM D695 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load (1.8 MPa, Unannealed) | 56.1 | °C | ASTM D648 |
| Thermoset | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Thermoset Components | |||
| Part A | Mix Ratio by Weight: 100, Mix Ratio by Volume: 4.0 | ||
| Part B | Mix Ratio by Weight: 24, Mix Ratio by Volume: 1.0 | ||
| Pot Life 4 | 11 | min | ASTM D2471 |
| Thermoset Mix Viscosity 5 | 1000 | cP | ASTM D2393 |
| Note Message | |
|---|---|
| 1 . | Thin Film |
| 2 . | 6 ply / 10 oz. laminate after 7 days at 73°F / 23°C |
| 3 . | 6 ply / 10 oz. laminate after 7 days at 73°F / 23°C |
| 4 . | 100 g |
| 5 . | 100 g |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REXtac® APAO RT 3315 | Huntsman Corporation | PAO | REXtac® APAO |
| Borealis PP BE375MO | Borealis AG | PP Copolymer | Borealis PP |
| Lionpol LC-62306 | Lion Polymers Incorporated | TPE | Lionpol |
| Petlon R-Prime O3-00-00-BK | Petlon Polymers Ltd | ABS+Nylon | Petlon R-Prime |
| OTECH CPE OTE4535 - Power Jacket | OTECH Corporation | CPE | OTECH CPE |