Next Nylon 66 Prime Series PMGHS40-01BK
| Category: | Nylon 66 , Polyamide 66 |
| Manufacturer: | Next Polymers Ltd. |
| Trademark: | Next Nylon 66 Prime Series |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vIii92_Next-Nylon-66-Prime-Series-PMGHS40-01BK.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Description PA66 Glass/Mineral Reinforced Heat stabilized Black compound Product Applications commonly used in Automotive industries to mould a large part such as rocker cover and Engine cover. Benefits Good combination Between thermal and Mechanical properties & low warpage. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| RoHS Compliance |
|
| Appearance |
|
| Processing Method |
|
| Physical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Specific Gravity | 1.47 | -- | g/cm³ | ASTM D792 |
| Molding Shrinkage | ASTM D955 | |||
| Flow | 0.40 | -- | % | |
| Across Flow | 0.95 | -- | % | |
| Water Absorption | ASTM D570 | |||
| 23°C, 24 hr | 1.5 | -- | % | |
| Saturation 1 | 5.0 | -- | % |
| Hardness | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Rockwell Hardness | ASTM D785 | |||
| M-Scale | 105 | -- | ||
| R-Scale | 120 | -- |
| Mechanical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Tensile Modulus | 9000 | 6200 | MPa | ASTM D638 |
| Tensile Strength | 140 | 95.0 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.0 | 5.0 | % | ASTM D638 |
| Flexural Modulus | 8800 | -- | MPa | ASTM D790 |
| Flexural Strength | 210 | -- | MPa | ASTM D790 |
| Impact | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Notched Izod Impact (23°C) | 59 | 88 | J/m | ASTM D256 |
| Thermal | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | |||
| 0.45 MPa, Unannealed | 255 | -- | °C | |
| 1.8 MPa, Unannealed | 240 | -- | °C | |
| Melting Temperature | 262 | -- | °C | ASTM D2117 |
| Electrical | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Surface Resistivity | 1.0E+16 | -- | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+17 | -- | ohms·cm | IEC 60093 |
| Electric Strength | 28 | -- | kV/mm | IEC 60243-1 |
| Comparative Tracking Index | > 450 | -- | V | IEC 60112 |
| Flammability | Dry | Conditioned | Unit | Test Method |
|---|---|---|---|---|
| Flame Rating (0.800 mm) | HB | -- | UL 94 |
| Injection | Dry | Unit | |
|---|---|---|---|
| Drying Temperature - Hot Air Dryer | 80.0 | °C | |
| Drying Time | 4.0 to 6.0 | hr | |
| Suggested Max Moisture | 0.20 | % | |
| Rear Temperature | 260 to 270 | °C | |
| Middle Temperature | 270 to 275 | °C | |
| Front Temperature | 275 to 280 | °C | |
| Mold Temperature | 85.0 to 95.0 | °C |
| Note Message | |
|---|---|
| 1 . | Immersed |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| POLYLAN T-015 | POLYMA Kunststoff GmbH & Co. KG | ABS | POLYLAN |
| SCHULAMID® 66GF25 | A. Schulman Inc. | Nylon 66 | SCHULAMID® |
| WPP PP WPP331 | Washington Penn Plastic Co. Inc. | PP Impact Copolymer | WPP PP |
| WEVO-CHEMIE Polyurethanes PU 590 FL/300 M | WEVO-CHEMIE GmbH | PUR, Unspecified | WEVO-CHEMIE Polyurethanes |
| Next Nylon 6 Prime Series NGF05-01BK | Next Polymers Ltd. | Nylon 6 | Next Nylon 6 Prime Series |