MALEX 01EFR002 - 6208
| Category: | PC , Polycarbonate |
| Manufacturer: | AD majoris |
| Trademark: | MALEX |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vI2TYv_MALEX-01EFR002---6208.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MALEX 01EFR002 - 6208 is a medium viscosity polycarbonate (PC) resin (UL94 V2) and contains a release agent to ensure easy processing, intended for injection moulding. The product is available in black (MALEX 01EFR002-8229) but other colours can be provided on request They combine high mechanical requiring rigidity, thermal and electrical properties with excellent chemical resistance and dimensional stability APPLICATIONS MALEX 01EFR002 - 6208 is intended for the injection moulding of electrical components and mechanical systems, such as:
|
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.20 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 12 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (Saturation, 23°C) | 0.35 | % | DIN 53495 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | 2350 | MPa | ISO 527-2/1 |
| Tensile Stress (Yield) | 63.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Break) | 110 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 2300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 73 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | No Break | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, Unannealed | 136 | °C | ISO 75-2/B |
| 1.8 MPa, Unannealed | 125 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 141 | °C | ISO 306/B50 |
| Ball Pressure Test (125°C) | Pass | IEC 60695-10-2 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | > 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | > 1.0E+15 | ohms·cm | IEC 60093 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.750 mm | V-2 | ||
| 6.00 mm | V-0 | ||
| Glow Wire Flammability Index (1.00 mm) | 850 | °C | IEC 60695-2-12 |
| Oxygen Index | 25 | % | ISO 4589-2 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 120 | °C | |
| Drying Time | 2.0 to 4.0 | hr | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 80.0 to 110 | °C | |
| Injection Rate | Fast |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSH 6054 | Marco Polo International, Inc. | PS (HIPS) | MARPOL® PSH |
| TRANSMARE® 14CT30-0.001 | Transmare Compounding B.V. | PP Copolymer | TRANSMARE® |
| UMERIT® 500F | UBE America, Inc. | LLDPE | UMERIT® |
| ACCUTECH™ NY0730G40L1 | ACLO Compounders Inc. | Nylon 6 | ACCUTECH™ |
| Hostaform® XGC25 | Celanese Corporation | Acetal (POM) Copolymer | Hostaform® |