LNP™ STAT-KON™ EE003XXC compound
| Category: | PEI , Polyether Imide |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ STAT-KON™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vGikxN_LNPSTATKONEE003XXCcompound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP STAT-KON EE003XXC is a compound based on Polyetherimide resin containing Carbon Fiber. Added features of this material include: Clean Compounding System. Also known as: LNP* STAT-KON* Compound EC-1003 CCS Product reorder name: EE003XXC |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.33 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (24 hr) | 0.10 - 0.30 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 165 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 1.6 | % | ASTM D638 |
| Flexural Modulus | 11700 | MPa | ASTM D790 |
| Flexural Strength | 248 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Unnotched Izod Impact (23°C) | 370 | J/m | ASTM D4812 |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+2 - 1.0E+6 | ohms | ASTM D257 |
| Volume Resistivity | 1.0E+2 - 1.0E+6 | ohms·cm | ASTM D257 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® PSM 6131 | Marco Polo International, Inc. | PS (MIPS) | MARPOL® PSM |
| S&E Wire & Cable GTPO8280 NATURAL | S&E Specialty Polymers, LLC | TPO (POE) | S&E Wire & Cable |
| Haysite BMC 18600 | Haysite Reinforced Plastics | Polyester, TS | Haysite BMC |
| Karina IVORY PVC COMPOUND -E 602D35/ 1-A-AT-IS | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| LEXAN™ HF1140R resin | SABIC Innovative Plastics | PC | LEXAN™ |