Pearlbond™ 12C75
| Category: | TPU-Polyester , Thermoplastic Polyurethane Elastomer (Polyester) |
| Manufacturer: | Lubrizol Advanced Materials, Inc. |
| Trademark: | Pearlbond™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vGgM6x_Pearlbond-12C75.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Pearlbond® 12C75 is polyester-based thermoplastic polyurethane, supplied in form of colourless, translucent granules, combining hardness with excellent low-temperature flexibility and a low softening point. Pearlbond® 12C75 is mainly used for making heat-sealable fabrics (thermobonding), obtained by coating processes such: -Hot Melt Coating system: Rotogravure hot melt printing. The product is melted in an extruder and then pumped into a deposit in front of the engraved roller. -Powder Coating system: Scattering or dot-coating (powder or paste). The product is previously ground into powder, by cryogenic grinding. The particle size of the powder will depend on the application technique to be used. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Agency Ratings |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | |||
| -- | 1.19 | g/cm³ | ASTM D792 |
| 20°C | 1.19 | g/cm³ | ISO 2781 |
| Melt Mass-Flow Rate (MFR) (177°C/2.16 kg) | 15 to 40 | g/10 min | ISO 1133 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Durometer Hardness (Shore A) | 78 | ASTM D2240, ISO 868 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ISO 527-2 | ||
| -- | 24.0 | MPa | |
| 100% Strain | 4.00 | MPa | |
| 300% Strain | 5.00 | MPa | |
| Tensile Strain (Break) | 650 | % | ISO 527-2 |
| Elastomers | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress | ASTM D412 | ||
| 100% Strain | 4.00 | MPa | |
| 300% Strain | 5.00 | MPa | |
| Tensile Strength | 24.0 | MPa | ASTM D412 |
| Tensile Elongation (Break) | 650 | % | ASTM D412 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melting Temperature | 130 to 140 | °C | Internal Method |
| Fill Analysis | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Melt Viscosity 1(160°C) | 1050 | Pa·s | ISO 1133 |
| Additional Information | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Softening Range | 110 to 130 | °C | Internal Method |
| Note Message | |
|---|---|
| 1 . | 2.16 Kg |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Maxelast® P2765 | Nantong Polymax Elastomer Technology, Co., Ltd | TPE | Maxelast® |
| TOTAL Polypropylene PPH 4022 | TOTAL Refining & Chemicals | PP Homopolymer | TOTAL Polypropylene |
| ACCUTECH™ HP0336W10L | ACLO Compounders Inc. | PP Homopolymer | ACCUTECH™ |
| Celanex® 4300LM | Celanese Corporation | PBT | Celanex® |
| INTOL® 1783 | Versalis S.p.A. | SBR, Emulsion | INTOL® |