Luxy® K3 G55
| Category: | Nylon 6 , Polyamide 6 |
| Manufacturer: | LG Chem Ltd. |
| Trademark: | Luxy® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vGaAXg_Luxy-K3-G55.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Luxy®K3 G55 is a polyamide 6 (nylon 6) material,. This product is available in North America, Latin America, Europe or Asia Pacific. The processing method is injection molding. Luxy®The main features of K3 G55 are:
Luxy®The typical application areas of K3 G55 are: electrical/electronic applications |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.50 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow (23°C, 3.20 mm) | 0.030 - 0.15 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.50 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Elongation 1(Break, 3.20 mm) | 6.0 | % | ASTM D638 |
| Flexural Modulus 2(3.20 mm) | 13000 | MPa | ASTM D790 |
| Flexural Strength 3(3.20 mm) | 281 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C, 6.40 mm) | 160 | J/m | ASTM D256 |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.800 mm | HB | UL 94 | |
| 1.60 mm | HB | UL 94 | |
| 2.50 mm | HB | UL 94 | |
| 3.20 mm | HB | UL 94 |
| Additional Information |
|---|
| All properties, except melt flow rate are measured on injection molulded specimens and after 48 hours storage at 23°C, 50% relative humidty. |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 - 100 | °C | |
| Drying Time | 4.0 - 5.0 | hr | |
| Rear Temperature | 280 - 300 | °C | |
| Middle Temperature | 280 - 300 | °C | |
| Front Temperature | 280 - 300 | °C | |
| Nozzle Temperature | 280 - 320 | °C | |
| Processing (Melt) Temp | 280 - 300 | °C | |
| Mold Temperature | 80.0 - 100 | °C | |
| Back Pressure | 29.4 - 58.8 | MPa | |
| Screw Speed | 50 - 150 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | 1.3 mm/min |
| 3 . | 1.3 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymer-E EV101 | Asia Polymer Corporation (APC) | EVA | Polymer-E |
| Radilon® BN 200 AS/2 | Radici Plastics | Nylon 6 | Radilon® |
| Siloxane Masterbatch MB40-006 | Multibase, A Dow Corning Company | Siloxane, UHMW | Siloxane Masterbatch |
| Vydyne® R535J BK0678 | Ascend Performance Materials Operations LLC | Nylon 66 | Vydyne® |
| Zhongfa POM GR-20 | Yuyao Zhongfa Engineering Plastics Co. Ltd. | Acetal (POM) Copolymer | Zhongfa |