Generic PP Impact Copolymer - Talc
| Category: | PP Impact Copolymer , Polypropylene Impact Copolymer |
| Manufacturer: | Generic |
| Trademark: | Generic |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vFznOt_Generic-PP-Impact-Copolymer---Talc.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
This data represents typical values that have been calculated from all products classified as: Generic PP Impact Copolymer - Talc This information is provided for comparative purposes only. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 0.978 - 1.24 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 4.0 - 13 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (23°C) | 0.89 - 1.3 | % | ASTM D955 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Yield, 23°C) | 21.8 - 27.9 | MPa | ASTM D638 |
| Tensile Elongation (Break, 23°C) | 8.0 - 36 | % | ASTM D638 |
| Flexural Modulus (23°C) | 1740 - 3290 | MPa | ASTM D790 |
| Flexural Strength (23°C) | 43.9 - 46.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact (23°C) | 18 - 60 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, not annealed | 104 - 141 | °C | ASTM D648 |
| 1.8 MPa, not annealed | 60.0 - 63.0 | °C | ASTM D648 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 82.5 - 93.3 | °C | |
| Drying Time | 1.5 - 3.0 | hr | |
| Processing (Melt) Temp | 215 - 232 | °C | |
| Mold Temperature | 18.3 - 60.0 | °C |
| Injection instructions |
|---|
| This data represents typical values that have been calculated from all products classified as: Generic PP Impact Copolymer - TalcThis information is provided for comparative purposes only. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Polymist® F5A | Solvay Specialty Polymers | PTFE | Polymist® |
| Vi-Chem PVC VIR 1874 | Vi-Chem Corporation | PVC, Unspecified | Vi-Chem PVC |
| Borealis LE6022 | Borealis AG | LDPE | Borealis |
| Iupilon® RS-1001R | Mitsubishi Engineering-Plastics Corp | PC | Iupilon® |
| Durethan® BKV 35 000000 | LANXESS GmbH | Nylon 6 | Durethan® |