TEKAPPO™ J100
| Category: | PPE+PS , Polyphenylene Ether + PS |
| Manufacturer: | Mando Advanced Materials Co., Ltd. |
| Trademark: | TEKAPPO™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vFkMWQ_TEKAPPO-J100.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| J100 is PPO/PS unreinforced product and low water absorption, hydrolytic stability, dimensional stability. |
| General Information | |
|---|---|
| Features |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.06 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (23°C, 24 hr) | 0.23 | % | ASTM D570 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1(Break) | 49.0 | MPa | ASTM D638 |
| Tensile Elongation 2(Break) | 28 | % | ASTM D638 |
| Flexural Modulus 3 | 2500 | MPa | ASTM D790 |
| Flexural Strength 4 | 89.2 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | ASTM D256 | ||
| -30°C, 3.18 mm | 49 | J/m | |
| 23°C, 3.18 mm | 180 | J/m |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 137 | °C | |
| 1.8 MPa, Unannealed | 126 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 105 to 110 | °C | |
| Drying Time | 3.0 to 4.0 | hr | |
| Rear Temperature | 250 to 300 | °C | |
| Middle Temperature | 260 to 305 | °C | |
| Front Temperature | 270 to 310 | °C | |
| Nozzle Temperature | 280 to 310 | °C | |
| Processing (Melt) Temp | 280 to 310 | °C | |
| Mold Temperature | 75.0 to 105 | °C |
| Note Message | |
|---|---|
| 1 . | 50 mm/min |
| 2 . | 50 mm/min |
| 3 . | 3.0 mm/min |
| 4 . | 3.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Hostalen PP H2222 36 | LyondellBasell Industries | PP Impact Copolymer | Hostalen PP |
| KOPLA PC KCG1010 | KOPLA Co., Ltd. | PC | KOPLA PC |
| Karina YELLOW PVC COMPOUND 800-02/42-RTC | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |
| Pebax® MV 1074 SA 01 MED | Arkema | PEBA-Ether | Pebax® |
| Sylvin 8474-80 Black | Sylvin Technologies Incorporated | PVC+NBR | Sylvin |