MAGNUM™ 3504
| Category: | ABS , ABS Resin |
| Manufacturer: | Trinseo |
| Trademark: | MAGNUM™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vFLQky_MAGNUM-3504.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
MAGNUM* 3504 is a general purpose resin and can be used for both injection moulding and extrusion applications. This grade combines high impact with medium-high heat resistance. The mass (continuous process) ABS technology ensures an ABS resin that combines excellent processability with a stable light base colour that is ideal for self-colouring. Applications:
|
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.05 | g/cm³ | ISO 1183/B |
| Apparent Density | 0.65 | g/cm³ | ISO 60 |
| Melt Mass-Flow Rate (MFR) (220°C/10.0 kg) | 5.2 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (220°C/10.0 kg) | 5.30 | cm³/10min | ISO 1133 |
| Molding Shrinkage - Flow | 0.40 to 0.70 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (3.20 mm, Injection Molded) | 2140 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 3.20 mm, Injection Molded) | 43.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield, 3.20 mm, Injection Molded) | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus (3.20 mm, Injection Molded) | 2050 | MPa | ISO 178 |
| Flexural Stress (3.20 mm, Injection Molded) | 65.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | |||
| -30°C, Injection Molded | 13 | kJ/m² | ISO 179/1eA |
| -30°C, Injection Molded | 9.0 | kJ/m² | ISO 179/2C |
| 23°C, Injection Molded | 23 | kJ/m² | ISO 179/1eA |
| 23°C, Injection Molded | 15 | kJ/m² | ISO 179/2C |
| Notched Izod Impact Strength | ISO 180/1A | ||
| -30°C, Injection Molded | 12 | kJ/m² | |
| 23°C, Injection Molded | 25 | kJ/m² |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Annealed) | 101 | °C | ISO 75-2/A |
| Vicat Softening Temperature | 102 | °C | ISO 306/B50 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Burning Rate 1(2.00 mm) | 55 | mm/min | ISO 3795 |
| Flame Rating 2 | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB | ||
| Carbon Emission | 30.0 | µg/g | VDA 277 |
| Fogging 3 | 98 | % | ISO 6452 |
| Note Message | |
|---|---|
| 1 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 2 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| 3 . | This rating not intended to reflect hazards presented by this or any other material under actual fire conditions. |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| REPOL® SRM250NC | Reliance Industries Limited | PP Random Copolymer | REPOL® |
| Sinelec CCB6005 | Teknor Apex Asia Pacific PTE. LTD. | PS (Specialty) | Sinelec |
| Axiall PVC 8150 White 209 | Axiall Corporation | PVC, Rigid | Axiall PVC |
| Garaflex™ E X 00-207F NAT UV-FG LCF | AlphaGary | TPE | Garaflex™ E |
| Rotuba CAB B9324 (4% Plasticizer) | Rotuba Extruders, Inc. | CAB | Rotuba CAB |