Jamplast JPPCABSI
| Category: | PC+ABS , Polycarbonate + ABS |
| Manufacturer: | Jamplast, Inc. |
| Trademark: | Jamplast |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vFILGV_Jamplast-JPPCABSI.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| JPPCABSI engineering resin is designed to offer a balance of properties between impact strength, heat resistance and processability. It offers better processability than polycarbonate while offering high impact strength at both room and low temperatures compared to ABS. With a deflection temperature under load (264 psi, unannealed) of 230°F, JPPCABSI also offers high heat resistance compared to ABS. JPPCABSI engineering resin has been used in automotive instrument panel and interior trim applications. |
| General Information | |
|---|---|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.13 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (230°C/3.8 kg) | 3.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow | 0.70 | % | ASTM D955 |
| Water Absorption | ASTM D570 | ||
| 23°C, 24 hr | 0.15 | % | |
| Equilibrium, 23°C, 50% RH | 0.32 | % |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 115 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength 1 | ASTM D638 | ||
| Yield | 53.1 | MPa | |
| Break | 44.8 | MPa | |
| Tensile Elongation 2(Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2340 | MPa | ASTM D790 |
| Flexural Strength (Yield) | 82.7 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact 3 | ASTM D256 | ||
| -40°C, 3.18 mm | 430 | J/m | |
| -29°C, 3.18 mm | 530 | J/m | |
| 23°C, 3.18 mm | 730 | J/m | |
| Instrumented Dart Impact 4 | ASTM D3763 | ||
| -29°C, 3.18 mm, Total Energy | 62.1 | J | |
| 23°C, 3.18 mm, Total Energy | 56.5 | J |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 1.8 MPa, Unannealed, 3.18 mm | 110 | °C | |
| 1.8 MPa, Annealed, 3.18 mm | 121 | °C | |
| CLTE - Flow (-40 to 82°C) | 7.4E-5 | cm/cm/°C | ASTM D696 |
| Note Message | |
|---|---|
| 1 . | Type I, 51 mm/min |
| 2 . | Type I, 51 mm/min |
| 3 . | 0.25 mm Notch Depth |
| 4 . | 3.39 m/sec |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| UNITIKA Nylon 6 A1022GFL60 (A) | UNITIKA Plastics Division | Nylon 6 | UNITIKA Nylon 6 |
| NEFTEKHIM PP 3840K (T2101F) | Nizhnekamskneftekhim Inc. | PP Homopolymer | NEFTEKHIM PP |
| Network Polymers PP PPB 25 0620 | Network Polymers, Inc. | PP Copolymer | Network Polymers PP |
| DAPCO™ 3041FR | Cytec Industries Inc. | Epoxy | DAPCO™ |
| Orgalloy® RS 6600 | Arkema | Nylon 66 Alloy | Orgalloy® |