Tufpet PBT G2810
| Category: | PBT , Polybutylene Terephthalate |
| Manufacturer: | Mitsubishi Rayon America Inc. |
| Trademark: | Tufpet |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vFDHXA_Tufpet-PBT-G2810.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Tufpet PBT G2810 is a Polybutylene Terephthalate (PBT) material filled with 10% glass fiber. It is available in North America for injection molding. Important attributes of Tufpet PBT G2810 are:
|
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Additive |
|
| Features |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.52 | g/cm³ | ASTM D792 |
| Molding Shrinkage - Flow | 0.40 to 1.6 | % | ASTM D955 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 119 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength | 80.4 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 3.5 | % | ASTM D638 |
| Flexural Modulus | 5100 | MPa | ASTM D790 |
| Flexural Strength | 132 | MPa | ASTM D790 |
| Coefficient of Friction | ASTM D1894 | ||
| vs. Itself - Dynamic | 0.13 | ||
| vs. Metal - Dynamic | 0.090 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 36 | J/m | ASTM D256 |
| Unnotched Izod Impact | 200 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 210 | °C | |
| 1.8 MPa, Unannealed | 190 | °C | |
| RTI Elec | UL 746 | ||
| 0.790 mm | 130 | °C | |
| 1.57 mm | 130 | °C | |
| 3.18 mm | 130 | °C | |
| RTI Imp | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 120 | °C | |
| RTI Str | UL 746 | ||
| 0.790 mm | 120 | °C | |
| 1.57 mm | 120 | °C | |
| 3.18 mm | 120 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 0.790 mm | V-0 | ||
| 1.57 mm | V-0 | ||
| 3.18 mm | V-0 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 140 | °C | |
| Drying Time | 2.0 | hr | |
| Rear Temperature | 230 to 260 | °C | |
| Middle Temperature | 230 to 260 | °C | |
| Front Temperature | 230 to 260 | °C | |
| Mold Temperature | 40.0 to 100 | °C | |
| Injection Pressure | 81.4 | MPa | |
| Screw Speed | 80 | rpm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| MARPOL® Homo 36.0 | Marco Polo International, Inc. | PP Homopolymer | MARPOL® Homo |
| Mytex® AS33K-02 | Mytex Polymers | TPO | Mytex® |
| NEOFLON™ EP-7000 | DAIKIN AMERICA, INC. | ETFE | NEOFLON™ |
| Adell Polyamide AR-13 | Adell Plastics, Inc. | Nylon 66 | Adell Polyamide |
| LNP™ THERMOCOMP™ Lexan_LGK3020 compound | SABIC Innovative Plastics Asia Pacific | PC | LNP™ THERMOCOMP™ |