MAJORIS EW317 - 7970
| Category: | PP, Unspecified , Polypropylene |
| Manufacturer: | AD majoris |
| Trademark: | MAJORIS |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vF3PQW_MAJORIS-EW317---7970.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
EW317 - 7970 is a 30% chemically coupled glass fibre/mineral reinforced polypropylene compound intended for injection moulding, in specific BMW colour Schwarz Fainnerbe L. EW317 - 7970 has been developed especially for the automotive applications requiring high UV stability such as external parts. EW317 - 7970 has high stiffness and good dimensional stability also at high temperatures. APPLICATIONS Products requiring high service temperature, high mechanical strength, high UV resistance and high dimensional stability. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.12 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) (230°C/2.16 kg) | 10 | g/10 min | ISO 1133 |
| Molding Shrinkage | 0.40 - 0.80 | % |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Yield) | 91.0 | MPa | ISO 527-2/50 |
| Tensile Strain (Yield) | 2.7 | % | ISO 527-2/50 |
| Flexural Modulus 1 | 5300 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 14 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength (23°C) | 48 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature | |||
| 0.45 MPa, not annealed | 159 | °C | ISO 75-2/B |
| 1.8 MPa, not annealed | 145 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 | |
| Glow Wire Flammability Index (2.00 mm) | 750 | °C | IEC 60695-2-12 |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 80.0 | °C | |
| Drying Time | 3.0 | hr | |
| Processing (Melt) Temp | 210 - 260 | °C | |
| Mold Temperature | 30.0 - 50.0 | °C | |
| Injection Rate | Moderate |
| Injection instructions |
|---|
| Holding pressure: 50 to 70% of the injection pressure |
| Note Message | |
|---|---|
| 1 . | 2.0 mm/min |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RheTech Thermoplastic Polyolefin FT2500-594UV | RheTech, Inc. | Polyolefin, Unspecified | RheTech Thermoplastic Polyolefin |
| XANTAR® MX 1001 | Mitsubishi Engineering-Plastics Corp | PC | XANTAR® |
| BESTNYL SE30VI01AH | Triesa Plastics | Nylon 66 | BESTNYL |
| Arak LLDPE HD5813EA | Shazand (Arak) Petrochemical Corporation | HDPE | Arak LLDPE |
| Karina GRAY COLOR CONCENTRATE 18/367-FC-LMP | Karina Ind. e Com. de Plásticos Ltda | PVC, Unspecified | Karina |