Devcon DFense Blok™ Fast Cure (FC)

Category:	Epoxy , Epoxy; Epoxide
Manufacturer:	Devcon
Trademark:	Devcon
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vEHGGL_Devcon-DFense-Blok-Fast-Cure-FC-.pdf
PRICE:	Order Products email sales@su-jiao.com

Wechat: WECHAT

WECHAT

Message

Alumina ceramic bead-filled epoxy system with outstanding wear and abrasion resistance for severe service conditions. Fast cure allows for repaired processing equipment to be returned to service in as little as 2 hours.

Intended Use:

Repair scrubbers, ash handling systems, pipe elbows, screens, chutes, chippers, bins, hoppers, bunkers, separators and digester tables. Protect exhausters, launderers, housing fans, crushers, breakers, and conveyor screws.

Product Features:

Fast cure for minimal downtime

Superior wear and abrasion resistance

Able to withstand impact

Resistant to a wide range of chemicals

Non-sagging

General Information
Filler / Reinforcement	Ceramic bead packing
Features	Impact resistance, good Fast curing Good wear resistance Good chemical resistance Good wear resistance
Uses	Repair Materials
Appearance	Grey

Physical	Nominal Value	Unit	Test Method
Specific Gravity	2.00	g/cm³
Specific Volume	0.499	cm³/g
Solid content- by Volume	100	%

Additional Information	Nominal Value	Unit	Test Method
Temperature Resistance
Dry	149	°C
Wet	60	°C
Tensile Shear Adhesion	19.1	MPa	ASTM D1002

Physical	Nominal Value	Unit	Test Method
Molding Shrinkage - Flow	0.080	%	ASTM D2566

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore D)	80		ASTM D2240

Mechanical	Nominal Value	Unit	Test Method
Flexural Strength	51.6	MPa	ASTM D790
Compressive Strength	49.5	MPa	ASTM D695

Thermal	Nominal Value	Unit	Test Method
CLTE - Flow	5.9E-5	cm/cm/°C	ASTM D696

Electrical	Nominal Value		Test Method
Dielectric Constant	45.0		ASTM D150

Thermoset	Nominal Value	Unit	Test Method
Thermoset Components
Component a	Mixing ratio by weight: 2.0 Mixing ratio by capacity: 2.0
Component B	Mixing ratio by weight: 1.0 Mixing ratio by capacity: 1.0
Pot Life (24°C)	15	min

Additional Information	Nominal Value	Unit	Test Method
Cured 7 days @ 75°F

Uncured Properties	Nominal Value	Unit	Test Method
Curing Time	10	hr

Resin Grade	Manufacturer	Category	Trademark
TRIREX® 3027U(M3)	Samyang Corporation	PC	TRIREX®
GAPEX® RPP10EA54NA	Ferro Corporation	PP, Unspecified	GAPEX®
KumhoSunny ABS 770SRS	Shanghai KumhoSunny Plastics Co., Ltd.	ABS	KumhoSunny ABS
MAJORIS ET300	AD majoris	PP, Unspecified	MAJORIS
MARPOL® LDC 712	Marco Polo International, Inc.	LDPE	MARPOL® LDC