Hostacom M4 N01 LG82767
| Category: | PP Homopolymer , Polypropylene Homopolymer |
| Manufacturer: | LyondellBasell Industries |
| Trademark: | Hostacom |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vCT6pg_HostacomM4N01LG82767.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
Hostacom M4 N01 LG82767 is a 40% talc filled PP homopolymer, with low melt flow and good detergent resistance. The product is also available as a customized color matched, pellet form. Product is UL listed. Please contact Basell for shrinkage recommendations.This grade is delivered in G82767 color version. Dry material before processing. This grade is not intended for medical, pharmaceutical, food, drinking water and all applications not listed in the supported list. For more information please contact our sales representatives. |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Appearance |
|
| Forms |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density (23°C) | 1.21 | g/cm³ | ISO 1183/A |
| Melt Mass-Flow Rate (MFR) (230°C/5.0 kg) | 11 | g/10 min | ISO 1133 |
| Melt Volume-Flow Rate (MVR) (230°C/5.0 kg) | 11.0 | cm³/10min | ISO 1133 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus (23°C) | 3600 | MPa | ISO 527-2 |
| Tensile Stress (Yield, 23°C) | 33.0 | MPa | ISO 527-2 |
| Tensile Strain (Yield, 23°C) | 4.0 | % | ISO 527-2 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength (23°C) | 3.5 | kJ/m² | ISO 179/1eA |
| Charpy Unnotched Impact Strength | ISO 179/1eU | ||
| 0°C | 15 | kJ/m² | ISO 179/1eU |
| 23°C | 30 | kJ/m² | ISO 179/1eU |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Heat Deflection Temperature (1.8 MPa, Unannealed) | 72.0 | °C | ISO 75-2/A |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.5 mm | HB | UL 94 | |
| 3.0 mm | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| RTP 200 D TFE 13 SI 2 Z | RTP Company | Nylon 612 | RTP |
| Shin-Etsu Elastomer KE-1950-30A/B | Shin-Etsu Silicones of America | Silicone Rubber, HTV | Shin-Etsu Elastomer |
| LEXAN™ 923 resin | SABIC Innovative Plastics | PC | LEXAN™ |
| LNP™ VERTON™ RVL29 compound | SABIC Innovative Plastics | Nylon 66 | LNP™ VERTON™ |
| NORYL™ PX9406P resin | SABIC Innovative Plastics Asia Pacific | PPE | NORYL™ |