Hylex® P1307 L1 HB
| Category: | PC , Polycarbonate |
| Manufacturer: | Entec Polymers |
| Trademark: | Hylex® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vCI9SB_Hylex-P1307-L1-HB.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| Polycarbonate, UV Stabilized, Low Flow, Mold Release, Water Clear |
| General Information | |
|---|---|
| Additive |
|
| Features |
|
| RoHS Compliance |
|
| Appearance |
|
| Forms |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.20 | g/cm³ | ASTM D792 |
| Melt Mass-Flow Rate (MFR) (300°C/1.2 kg) | 7.0 | g/10 min | ASTM D1238 |
| Molding Shrinkage - Flow (3.18 mm) | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption (24 hr) | 0.15 | % | ASTM D570 |
| Hardness | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Rockwell Hardness (R-Scale) | 118 | ASTM D785 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Strength (Break) | 62.1 | MPa | ASTM D638 |
| Tensile Elongation (Break) | 130 | % | ASTM D638 |
| Flexural Modulus | 2310 | MPa | ASTM D790 |
| Flexural Strength | 93.1 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | 850 | J/m | ASTM D256 |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | ASTM D648 | ||
| 0.45 MPa, Unannealed | 135 | °C | |
| 1.8 MPa, Unannealed | 124 | °C |
| Flammability | Nominal Value | Test Method | |
|---|---|---|---|
| Flame Rating | UL 94 | ||
| 1.50 mm | HB | ||
| 3.00 mm | HB |
| Optical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Refractive Index | 1.586 | ASTM D542 | |
| Transmittance | 88.0 | % | ASTM D1003 |
| Haze | 1.0 | % | ASTM D1003 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| SUSTAMID 6 ESD 60 | Röchling Sustaplast SE & Co. KG | Nylon 6 | SUSTAMID |
| TAIRIPRO F2003 | Formosa Plastics Corporation | PP Homopolymer | TAIRIPRO |
| Vipel® K190-RTM-17 | AOC, L.L.C. | Polyester Alloy | Vipel® |
| Dryflex® 602650S | ELASTO | SEBS | Dryflex® |
| LNP™ LUBRICOMP™ DL003EU compound | SABIC Innovative Plastics | PC | LNP™ LUBRICOMP™ |