| Category: | Acetal (POM) Copolymer , Acetal (POM) Copolymer |
| Manufacturer: | Korea Engineering Plastics Co., Ltd |
| Trademark: | Kepital® |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vAA8Zl_KepitalF3051.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
| UV resistance with UV carbon black, low viscosity grade, good for weather resistance purpose. It has stability on UV light, and so good at out-door use. |
| General Information | |
|---|---|
| Features |
|
| Uses |
|
| Appearance |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Density | 1.41 | g/cm³ | ISO 1183 |
| Melt Mass-Flow Rate (MFR) | 25 | g/10 min | ISO 1133 |
| Molding Shrinkage - Flow (3.00 mm) | 2.0 | % | ISO 294-4 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Stress (Break, 23°C) | 59.0 | MPa | ISO 527-2 |
| Nominal Tensile Strain at Break (23°C) | 35 | % | ISO 527-2 |
| Flexural Modulus (23°C) | 2650 | MPa | ISO 178 |
| Flexural Stress (23°C) | 86.0 | MPa | ISO 178 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Charpy Notched Impact Strength | 7.0 | kJ/m² | ISO 179/1eA |
| Electrical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Surface Resistivity | 1.0E+15 | ohms | IEC 60093 |
| Volume Resistivity | 1.0E+14 | ohms·cm | IEC 60093 |
| Dielectric Strength | 19 | kV/mm | IEC 60243-1 |
| Flammability | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Flame Rating | HB | UL 94 |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Moplen S30SW | Shazand (Arak) Petrochemical Corporation | PP Homopolymer | Moplen |
| CALP E4331 | Lion Idemitsu Composites Co., Ltd. | Polyolefin, Unspecified | CALP |
| Dryflex® 660480 | ELASTO | TPE | Dryflex® |
| Halar® 513LC | Solvay Specialty Polymers | ECTFE | Halar® |
| OTECH TPO OTR8588 - Gasket | OTECH Corporation | TPE | OTECH TPO |