Sarlink® TPE RV-2670D Datasheet,TPE,Teknor Apex Company-SHANGHAI SUSHENG

Message
Sarlink RV-2670D is a high performance thermoplastic elastomer, available in NAT and BLK, used in a variety of transportation applications. Sarlink RV-2670D is a high hardness, high density, filled grade with a 400k psi modulus that is UV stabilized and suitable for extrusion and injection molding.

General Information
Features	Sunlight Resistant High specific gravity High density smoothness Light stabilization Good UV resistance Good adhesion Low liquidity Good chemical resistance Good weather resistance Good toughness Lubrication Fill High hardness
Uses	Application in Automobile Field Automotive exterior parts Car exterior decoration Bracket
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Extrusion Injection molding

Physical	Nominal Value	Unit	Test Method
Density	1.18	g/cm³	ISO 1183
Melt Mass-Flow Rate (MFR) (230°C/2.16 kg)	2.0	g/10 min	ASTM D1238

Hardness	Nominal Value	Test Method
Durometer Hardness		ISO 868
Shore D, 1 second, injection molding	70	ISO 868
Shore D, 5 seconds, injection molding	69	ISO 868
Shore D, 15 seconds, injection molding	68	ISO 868

Mechanical	Nominal Value	Unit	Test Method
Flexural Modulus	2690	MPa	ASTM D790

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress ¹			ISO 37
Transverse flow : 100% strain	12.8	MPa	ISO 37
Flow : 100% strain	17.2	MPa	ISO 37
Tensile Stress ²			ISO 37
Transverse flow : Fracture	17.9	MPa	ISO 37
Flow : Fracture	21.8	MPa	ISO 37
Tensile Elongation ³			ISO 37
Transverse flow : Fracture	120	%	ISO 37
Flow : Fracture	140	%	ISO 37
Tear Strength ⁴			ISO 34-1
Transverse flow	180	kN/m	ISO 34-1
Flow	130	kN/m	ISO 34-1
Compression Set ⁵			ISO 815
23°C, 22 hr	67	%	ISO 815
70°C, 22 hr	94	%	ISO 815
90°C, 70 hr	93	%	ISO 815

Aging	Nominal Value	Unit	Test Method
Change in Tensile Strength in Air ⁶			ISO 188
Transverse flow : 110°C, 1008 hr	6.1	%	ISO 188
Flow : 110°C, 1008 hr	11	%	ISO 188
Transverse flow : 100% strain 110°C, 1008 hr	16	%	ISO 188
Flow : 100% strain 110°C, 1008 hr	29	%	ISO 188
Transverse flow : 125°C, 168 hr	3.9	%	ISO 188
Flow : 125°C, 168 hr	7.9	%	ISO 188
Transverse flow : 100% strain 125°C, 168 hr	20	%	ISO 188
Flow : 100% strain 125°C, 168 hr	33	%	ISO 188
Change in Tensile Strain at Break in Air ⁷			ISO 188
Transverse flow : 110°C, 1008 hr	-31	%	ISO 188
Flow : 110°C, 1008 hr	-18	%	ISO 188
Transverse flow : 125°C, 168 hr	16	%	ISO 188
Flow : 125°C, 168 hr	9.2	%	ISO 188
Change in Shore Hardness in Air			ISO 188
Support d, 110°C, 1008 hr ⁸	1.4		ISO 188
Support d, 110°C, 1008 hr ⁹	1.2		ISO 188
Support d, 110°C, 1008 hr ¹⁰	0.60		ISO 188
Support d, 125°C, 168 hr ¹¹	1.3		ISO 188
Support d, 125°C, 168 hr ¹²	1.1		ISO 188
Support d, 125°C, 168 hr ¹³	0.10		ISO 188

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 206 sec^-1)	613	Pa·s	ASTM D3835

Legal statement
The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Legal statement

The information and recommendations contained in this bulletin are, to the best of our knowledge, accurate and reliable but no guarantee of their accuracy is made. All products are sold upon condition that purchasers shall make their own tests to determine the suitability of such products for their particular purposes and uses and purchaser assumes all risks and liability for the results of use of the products, including use in accordance with seller's recommendations. Nothing in this bulletin constitutes permission or a recommendation to practice or use any invention covered by any patent owned by this company or others. There is no warranty of merchantability and there are no other warranties for the products described. For detailed Product Stewardship information, please contact us. Any product of Teknor Apex, including product names, shall not be used or tested in medical or food contact applications without the prior written acknowledgement of Teknor Apex as to the intended use. Please note that some products may not be available in one or more countries.

Injection	Nominal Value	Unit
Rear Temperature	193 - 232	°C
Middle Temperature	193 - 232	°C
Front Temperature	193 - 232	°C
Nozzle Temperature	193 - 232	°C
Processing (Melt) Temp	193 - 232	°C
Mold Temperature	16 - 43	°C
Injection Pressure	1.38 - 6.89	MPa
Injection Rate	Moderate-Fast
Back Pressure	0.172 - 0.345	MPa
Screw Speed	50 - 100	rpm
Cushion	3.81 - 25.4	mm

Extrusion	Nominal Value	Unit
Cylinder Zone 1 Temp.	193 - 221	°C
Cylinder Zone 2 Temp.	193 - 221	°C
Cylinder Zone 3 Temp.	193 - 221	°C
Cylinder Zone 4 Temp.	193 - 221	°C
Cylinder Zone 5 Temp.	193 - 221	°C
Die Temperature	193 - 221	°C

Extrusion instructions
Screw Speed: 30 to 100 rpm

Note Message
1 .	Type 1, 510mm/min
2 .	Type 1, 510mm/min
3 .	Type 1, 510mm/min
4 .	B method, right angle specimen (without cut), 510mm/min
5 .	Type a
6 .	Type 1
7 .	Type 1
8 .	15 sec
9 .	5 sec
10 .	1 sec
11 .	1 sec
12 .	5 sec
13 .	15 sec

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	Teknor Apex Company
Trademark:	Sarlink® TPE
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	vA6UD8_SarlinkTPERV2670D.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sanren EVA 7.5/1.5	SINOPEC Shanghai Petrochemical Co. Ltd.	EVA	Sanren
ADENE OCTEG	A.D. Compound spa	PP Copolymer	ADENE
Cheng Yu A706G1	Cheng Yu Plastic Company Limited	SAN	Cheng Yu
EMOPLEN® HP GFR 30	EMAS Plastik San.Tic.AS.	PP Homopolymer	EMOPLEN®
Globalene® ST866K	Lee Chang Yung Chemical Industry Corp.	PP Random Copolymer	Globalene®