LNP™ LUBRICOMP™ DX07404H compound
| Category: | PC , Polycarbonate |
| Manufacturer: | SABIC Innovative Plastics |
| Trademark: | LNP™ LUBRICOMP™ |
| Fillers: | - |
| Ports: | Qinzhou, Shekou, Shanghai, Ningbo |
| Delivery Terms | FOB, CIF, DAP, DAT, DDP |
| PDF: | vA3TGX_LNP-LUBRICOMP-DX07404H-compound.pdf  |
| PRICE: | Order Products email sales@su-jiao.com |
Wechat:
| Message |
|---|
|
LNP LUBRICOMP DX07404H is a compound based on Polycarbonate containing Proprietary Fillers. Added features of this grade are: Healthcare, Wear Resistant. Also known as: LNP* LUBRICOMP* Compound DX07404H Product reorder name: DX07404H |
| General Information | |
|---|---|
| Filler / Reinforcement |
|
| Features |
|
| Uses |
|
| Processing Method |
|
| Physical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Specific Gravity | 1.25 | g/cm³ | ASTM D792 |
| Molding Shrinkage | |||
| Flow | 0.40 to 0.60 | % | Internal Method |
| Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Across Flow | 0.50 to 0.70 | % | Internal Method |
| Across Flow : 24 hr | 0.50 to 0.70 | % | ASTM D955 |
| Water Absorption | |||
| 24 hr, 50% RH | 0.14 | % | ASTM D570 |
| Equilibrium, 23°C, 50% RH | 0.18 | % | ISO 62 |
| Mechanical | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Tensile Modulus | |||
| -- 1 | 2490 | MPa | ASTM D638 |
| -- | 2270 | MPa | ISO 527-2/1 |
| Tensile Strength | |||
| Yield 2 | 60.0 | MPa | ASTM D638 |
| Yield | 59.0 | MPa | ISO 527-2/5 |
| Break 3 | 50.0 | MPa | ASTM D638 |
| Break | 49.0 | MPa | ISO 527-2/5 |
| Tensile Elongation | |||
| Yield 4 | 5.0 | % | ASTM D638 |
| Yield | 5.0 | % | ISO 527-2/5 |
| Break 5 | 54 | % | ASTM D638 |
| Break | 58 | % | ISO 527-2/5 |
| Flexural Modulus | |||
| 50.0 mm Span 6 | 2380 | MPa | ASTM D790 |
| -- 7 | 2380 | MPa | ISO 178 |
| Flexural Stress | |||
| -- | 81.0 | MPa | ISO 178 |
| Break, 50.0 mm Span 8 | 89.0 | MPa | ASTM D790 |
| Impact | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Notched Izod Impact | |||
| 23°C | 130 | J/m | ASTM D256 |
| 23°C 9 | 11 | kJ/m² | ISO 180/1A |
| Unnotched Izod Impact Strength 10(23°C) | 180 | kJ/m² | ISO 180/1U |
| Thermal | Nominal Value | Unit | Test Method |
|---|---|---|---|
| Deflection Temperature Under Load | |||
| 0.45 MPa, Unannealed, 3.20 mm | 135 | °C | ASTM D648 |
| 0.45 MPa, Unannealed, 64.0 mm Span 11 | 135 | °C | ISO 75-2/Bf |
| 1.8 MPa, Unannealed, 3.20 mm | 124 | °C | ASTM D648 |
| 1.8 MPa, Unannealed, 64.0 mm Span 12 | 125 | °C | ISO 75-2/Af |
| CLTE | ASTM D696 | ||
| Flow : -30 to 30°C | 6.4E-5 | cm/cm/°C | |
| Transverse : -30 to 30°C | 6.5E-5 | cm/cm/°C |
| Injection | Nominal Value | Unit | |
|---|---|---|---|
| Drying Temperature | 121 | °C | |
| Drying Time | 4.0 | hr | |
| Drying Time, Maximum | 48 | hr | |
| Suggested Max Moisture | 0.020 | % | |
| Rear Temperature | 293 to 304 | °C | |
| Middle Temperature | 310 to 321 | °C | |
| Front Temperature | 321 to 332 | °C | |
| Processing (Melt) Temp | 304 to 327 | °C | |
| Mold Temperature | 82.2 to 110 | °C | |
| Back Pressure | 0.172 to 0.344 | MPa | |
| Screw Speed | 30 to 60 | rpm |
| Note Message | |
|---|---|
| 1 . | 5.0 mm/min |
| 2 . | Type I, 5.0 mm/min |
| 3 . | Type I, 5.0 mm/min |
| 4 . | Type I, 5.0 mm/min |
| 5 . | Type I, 5.0 mm/min |
| 6 . | 1.3 mm/min |
| 7 . | 2.0 mm/min |
| 8 . | 1.3 mm/min |
| 9 . | 80*10*4 |
| 10 . | 80*10*4 |
| 11 . | 80*10*4 mm |
| 12 . | 80*10*4 mm |
| Resin Grade | Manufacturer | Category | Trademark |
|---|---|---|---|
| Medalist® MD-12337 | Teknor Apex Company | TPE | Medalist® |
| Sindustris PBT GP2307FY | Sincerity Australia Pty Ltd. | PBT | Sindustris PBT |
| TechnoDur PBT 4 black (9996) | TechnoCompound GmbH | PBT | TechnoDur |
| Spartech Polycom WI8940FR-90 | Spartech Polycom | PVC Alloy | Spartech |
| WELLAMID Nylon 6000/42 GV 15 HWUVCP | CP-Polymer-Technik GmbH & Co. KG | Nylon 6 | WELLAMID Nylon |