Versaflex™ CE 3180 is targeted for consumer electronics applications where excellent abrasion resistance, chemical resistance and silky feel are required. Versaflex™ CE 3180 can also overmold to a variety of substrates including PC, ABS, PC/ABS, and Copolyester.

General Information
Features	Low friction coefficient Good UV resistance Workability, good Good coloring Good wear resistance Good chemical resistance Good appearance
Uses	overmolding Thin wall parts Computer components Electrical/Electronic Applications Electrical appliances Thick wall fittings (parts) Soft touch application Soft handle Communication application Consumer goods application field
RoHS Compliance	RoHS compliance
Appearance	Black Natural color
Forms	Particle
Processing Method	Injection molding

Physical	Nominal Value	Unit	Test Method
Specific Gravity	1.17	g/cm³	ASTM D792
Molding Shrinkage - Flow (193°C)	0.60 - 1.2	%	ASTM D955

Hardness	Nominal Value	Unit	Test Method
Durometer Hardness (Shore A, 10 sec)	79		ASTM D2240

Elastomers	Nominal Value	Unit	Test Method
Tensile Stress (300% Strain, 23°C)	8.00	MPa	ASTM D412
Tensile Strength (Break, 23°C)	16.0	MPa	ASTM D412
Tensile Elongation (Break, 23°C)	580	%	ASTM D412

Fill Analysis	Nominal Value	Unit	Test Method
Apparent Viscosity (200°C, 11200 sec^-1)	23.0	Pa·s	ASTM D3835

Additional Information	Nominal Value	Unit	Test Method
Mass Loss - 500 Cycle Abrasion Resistance ¹(23°C)	2.0	mg	ASTM D3389

Injection	Nominal Value	Unit
Drying Temperature	52 - 60	°C
Drying Time	3.0 - 4.0	hr
Suggested Max Moisture	< 0.030	%
Suggested Max Regrind	20	%
Rear Temperature	171 - 182	°C
Middle Temperature	182 - 210	°C
Front Temperature	188 - 216	°C
Nozzle Temperature	193 - 221	°C
Processing (Melt) Temp	193 - 218	°C
Mold Temperature	13 - 29	°C
Back Pressure	0.00 - 0.345	MPa
Screw Speed	50 - 100	rpm

Injection instructions
Typical colorant letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Contact GLS for more information on appropriate color concentrate base resins.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Versaflex™ CE 3180 should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 500 to 1,000 psi2nd Stage - Hold Pressure: 20-60% of BoostHold Time (Thick Part): 2 to 4 secHold Time (Thin Part): 1 to 2 sec

Injection instructions

Typical colorant letdown ratios are 50:1 to 25:1 - loading levels should be as low as possible to minimize the effect on adhesion. A high color match consistency can be obtained by the use of precolored compounds available from GLS. Concentrates based on PVC should not be used. The final determination of color concentrate suitability should be determined by customer trials. Contact GLS for more information on appropriate color concentrate base resins.Purge thoroughly before and after use of this product with a low flow (0.5 - 2.5 MFR) polyethylene (PE) or polypropylene (PP).Versaflex™ CE 3180 should not be left in the barrel for extended idle periods (greater than 5 minutes).Suggested Dewpoint: -40°FInjection Speed: 0.5 to 2 in/sec1st Stage - Boost Pressure: 500 to 1,000 psi2nd Stage - Hold Pressure: 20-60% of BoostHold Time (Thick Part): 2 to 4 secHold Time (Thin Part): 1 to 2 sec

Note Message
1 .	Abrasion wheel: H-18Mass Lost

Category:	TPE , Thermoplastic Elastomer
Manufacturer:	PolyOne Corporation
Trademark:	Versaflex™
Fillers:	-
Ports:	Qinzhou, Shekou, Shanghai, Ningbo
Delivery Terms	FOB, CIF, DAP, DAT, DDP
PDF:	v9o5Iw_VersaflexCE3180.pdf
PRICE:	Order Products email sales@su-jiao.com

Resin Grade	Manufacturer	Category	Trademark
Sindustris PBT GP2307FI	Sincerity Australia Pty Ltd.	PBT	Sindustris PBT
Vital-Line SHM8505	Teknor Apex Asia Pacific PTE. LTD.	PVC, Flexible	Vital-Line
3M™ Dyneon™ Fluoroelastomer FC 2120	3M Advanced Materials Division	Fluorelastomer	3M™ Dyneon™ Fluoroelastomer
Grivory® XE 5107 (GVL-5H V0)	EMS-GRIVORY	Nylon 66+Nylon 6I/X	Grivory®
Hanwha Total PP BI961	HANWHA TOTAL PETROCHEMICALS Co., Ltd.	PP Impact Copolymer	Hanwha Total PP